In this thesis, PVC/SAN blends, PVC/αMSAN blends and PVC/αMSAN/SAN blends were prepared by melt extrusion via miscibility and properties of the blends were investigated.
In chapter 2, we studied the rheological, mechanical and physical properties based on PVC DP variables and contents of CPVC. It had been determined that equilibrium torque and degradation time from PVC DP 1,000 is a guideline for good processing property. High DP PVC and high contents of CPVC were predicted that very difficult to process. However, high DP PVC gives excellent improvement on flexural strength and modulus and CPVC make excellent improvement on tensile strength and thermal resistance property, but adverse effects on specific gravity. In chapter 3, we investigated the rheological properties of the PVC/SAN blends and PVC/αMSAN blends prepared by melt extrusion. The PVC/SAN and $PVC/αMSAN blends have good processing properties. The miscibility of PVC/SAN blends and PVC/αMSAN blends were studied by DSC, DMTA, SEM, and ARES. The SAN series are immiscible with PVC, whereas αMSAN having 31wt% AN is miscible with PVC, even if blended by the melt extrusion due to the strong interaction between PVC and αMSAN.
In chapter 4, we studied the miscibility and properties of PVC/αMSAN blends by changing blends ratio and also studied the miscibility and properties of PVC/αMSAN blends by changing PVC. The PVC/αMSAN blends by changing blend ratios have good processing properties, good properties, and show good miscibility over all blend ratios. Due to the strong interaction between PVC and αMSAN, the high DP PVC/αMSAN blends have good rheological properties and the mechanical and physical properties of the blends are highly improved as PVC DP increased.
In chapter 5, we studied the miscibility of PVC/αMSAN/SAN blends using DSC, DMTA, SEM and ARES. The results indicate that the blends of PVC/αMSAN /SAN blends show different miscibility by AN contents of SAN. Due to the strong interaction between PVC and αMSAN, the PVC/αMSAN /SAN24 and PVC/αMSAN/SAN27 blends show improved miscibility comparing to PVC/SAN24 and PVC/SAN27 blends whereas PVC/αMSAN /SAN24 blends show same immiscibility to PVC/SAN31.
본 연구에서는, 용융압출로 PVC/SAN 브렌드, PVC/αMSAN 브렌드, PVC/αMSAN/SAN 브렌드를 만들어 상용성과 제반물성을 살펴보았다.
2 장에서는 PVC의 중합도와 CPVC의 함량에 따른 유변성질, 기계적성질과 물리적 성질을 연구하였다. PVC 중합도 1000이 가지는 평형토크와 탄화시간을 가공이 가능한 가이드라인으로 결정하였고, 중합도 1300 이상의 고중합도 PVC와 높은 함량의 CPVC는 가공을 어렵게 하는 것으로 예측되어졌다. 하지만 고중합도 PVC는 굴곡성질을 많이 개선시키며, CPVC는 인장강도와 열변형온도 개선에 좋은 영향을 주나 비중을 높이는 역효과가 있다. 3장에서는 용융압출로 준비한 PVC/SAN 브렌드와 PVC/αMSAN 브렌드의 상용성과 제반성질에 살펴보았다. PVC/SAN 브렌드와 PVC/αMSAN 브렌드는 순수 PVC보다 좋은 가공성을 가진다. PVC/SAN 브렌드와 PVC/αMSAN 브렌드의 상용성을 DSC, DMTA, SEM, ARES로 살펴본 결과, AN함량에 상관없이 SAN은 PVC와 상용성이 떨어지나 αMSAN 은 PVC와의 강한 상호작용으로 인해 용융압출로도 좋은 상용성을 보이는 것으로 나타났다.
4장에서는 브렌드 비율에 따른 PVC/αMSAN 브렌드의 상용성과 제반물성에 대해 연구하였고 또한 PVC 종류에 따른 PVC/αMSAN 브렌드의 상용성과 물성에 대해 연구하였다. 브렌드 비율에 따른 실험에서 PVC/αMSAN 브렌드는 모든 브렌드 비율에서 좋은 가공성, 물성, 상용성을 가지는 것으로 나타났다. PVC 종류에 따른 실험에서 αMSAN 의 PVC와의 강한 상호작용으로 인해, 고중합도 PVC/αMSAN 브렌드도 좋은 가공성과 상용성을 보이는 것으로 나타났으며 기계적, 물리적 성질이 크게 향상되는 것으로 나타났다.
5장에서는 PVC/αMSAN/SAN 브렌드의 상용성을 평가하였다. SAN의 AN 함량 에 따라 PVC/αMSAN/SAN 브렌드의 상용성이 달라지는 것으로 나타났다. αMSAN 의 PVC와의 강한 상호작용으로 인해, PVC/αMSAN/SAN24 와 PVC/αMSAN/SAN27 브렌드는 PVC/SAN24와 PVC/SAN27 브렌드에 비해 우수한 상용성을 보이나, PVC/αMSAN/SAN31 브렌드는 PVC/SAN31 브렌드와 같이 비상용성을 가지는 것으로 나타났다.