The branched monoalkoxy-substituted poly[2-(2-ethylhexyloxy)-1,4-phenylenevinylene] (EH-PPV) was prepared in thin films via the water-soluble precursor technique and solution elimination method. Poly[2-bromo-5-(2-ethylhexyloxy)-1,4-phenylenevinylene] (BEH-PPV) was also prepared via the water-soluble precursor technique and thermal elimination method. These polymers were characterized using UV-visible, FT-IR spectroscopy and DSC, TGA thermal analyzer. These precursor polymer films could be stretched up to 8 times, and the drawn films of the EH-PPV and BEH-PPV could be doped with $I_2$ and $FeCl_3$ to give conductivities of $10^{-1}\sim10^{-4}$S/cm. The third-order nonlinear optical susceptibility of the EH-PPV was determined by using third harmonic generation (THG) method at 1907 nm, fundamental wavelength. Measured $\chi^{(3)}$(-3ω; ω,ω,ω) value was 3.8×$10^{-12}$ esu. The maximum emission wavelength of EH-PPV film in photoluminescence spectrum was 560 nm and in the case of BEH-PPV 562 nm The color of PL spectra of two materials was yellowish-red.
곁가지 달린 모노알콕시가 치환된 폴리 [2-(2-에틸헥실옥시)-1,4-페닐렌비닐렌](EH-PPV) 은 수용성 선중합체 방법과 수용액 제거 반응을 통해 박막으로 합성하였다. 그리고 폴리 [2-브로모-5-(2-에틸헥실옥시) -1,4-페닐렌비닐렌] (BEH-PPV) 은 수용성 선중합체 방법으로 합성하였다. 수용액 제거반응으로 합성된 EH-PPV 의 경우 유기 용매인 메틸렌클로라이드, 트리클로로벤젠, 테트라하이드로퓨란등에 용해 가능하다. 그러므로, 이 폴리머는 열처리 없이도 전기발광소자에 발광층으로 사용 할 수 있다. BEH-PPV 의 광 발광 스펙트럼은 EH-PPV 의 스펙트럼과 비슷하였다. 그러므로 브롬의 전자 끄는 효과는 크지 않음을 알수 있다. EH-PPV 와 BEH-PPV은 560 nm 과 562 nm 에서 최대 발광을 보였다. 이 두 물질의 발광 색깔은 주황색에 해당된다. 3차 조합파 방법으로 EH-PPV 의 3차 비선형 광학계수를 측정 하였다. 측정된 3차 비선형 광학계수는 3.8×$10^{-12}$ esu 이었다. EH-PPV 와 BEH-PPV 의 연신시키지 않은, 연신시킨 박막은 $I_2$ 와 $FeCl_3$ 에 도핑되었고 전도도는 $10^{-1}~10^{-4}$ S/cm 로 나타났다.