To achieve adhesion between two arbitrary soft substrates, a curable nano-adhesive was developed via iCVD process. The nano adhesive is a copolymer of allyl glycidyl acrylate(AGE) and 2-hydroxyethyl acrylate(HEA) which was designed epoxy ring open reaction by hydroxyl group. pAH2 which was optimized by adhesion and solvent resistance test has 393 % stretchability with 87.5 kPa elastic modulus after annealing. Also, synthesized adhesive has high transmittance and excellent adhesion by only 500 nm thickness. By vapor deposition method, interpenetrating polymer network(IPN) was created between soft substrate and pAH2. Compared to commercial stretchable adhesives which were silbione and 3M VHB tape, pAH2 shows distinctly strong adhesion with structural failure. By crosslinking formation, adhesion between PDMS and eco-flex was 4.6 N/cm and maintained up to 90 % value after stretching test (30 % strain, 10^5 time) and solvent test (saline solution, 38 ℃ 1 week).
임의의 연성 기판 접착을 위해 iCVD 공정을 통해 연신성 나노 접착제를 개발 하였다. 나노 접착제는 allyl glycidyl acrylate(AGE) 와 2-hydroxyethyl acrylate(HEA)의 공중합체이며 hydroxyl 기가 epoxy 기를 열어 가교반응을 진행하는 시스템이다. 가장 높은 접쳑력[접착력]과 용매 저항성을 가지고 있는 pAH2 를 합성하였고 이는 가교 이후 87.5 kpa 의 elastic modulus 와 393 % 연신가능한 물성을 가지고 있다. 본 연구에서 합성시 soft 기판과 접착제 사이에 IPN 구조가 형성되어 있고 이점이 계면간의 접착력을 향상시켜 준다는 점을 확인하였다. 적절한 가교를 통해 향상된 응집력과 iCVD 공정으로 야기된 IPN 의 계면 접착력의 향상은 500 nm 의 두께 만으로 다양한 기판에서 반복적인 연신 실험(10 만번) 및 용매 실험(식염수, 7 일) 이후에도 접착력을 유지하게 만들어 주었다. 본 연구에서 개발된 접착제를 이용하면 soft 기판 접착시 기판 파단이 이루어질 정도의 강한 접착력이 부여된다. 특히 PDMS-eco flex 의 경우 4.6 N/cm 의 접착력이 측정 및 기판 파단이 이루어질 정도의 강한 접착력이다.