Polyethylene terephthalate (PET) film is a functional film with various protective properties such as its thermal stability, dimensional stability, high tensile strength, chemical stability, transparency, and gas impermeability. PET film usually composed of multiple layers to enhance the physical properties and grant various functionality. One of the commonly widely used PET film is polydimethylsiloxane (PDMS) coated PET film, which is widely used as a release liner to protect the surface of commercial products such as optically clear adhesive (OCA), wafer, flat panel display and printed flexible circuit because PDMS has excellent release properties such as hydrophobic surface, electrical insulation, flexibility, thermal stability and chemical stability. However, recycling of PDMS-coated PET film is difficult unless PDMS layer is removed from the PET film. In this work, a pretreatment process for removal of PDMS layer from the PET film by physical detachment of swollen PDMS is proposed. As the result, the amount of PDMS on the surface of PET film was decreased to 1%, suggesting that PDMS layer was successfully removed from PET film. As a result of glycolysis of pretreated film, the yield of bis(2-hydoxyethyl terephthalate) (BHET) was 85.24%. Pretreatment enables the recycling of PDMS-coated PET film waste.
Poly(ethylene terephthalate) (PET) 필름은 열적 안정성, 치수 안정성, 높은 인장강도, 화학적 안정성, 투명성, 가스 비침투성과 같이 안정한 기능성 필름이다. PET 필름은 물리적 안정성을 증가시키고, 여러 기능성을 부여하기 위해서 보통 여러 개의 층으로 이루어져 있다. 가장 많이 이용되는 다층 PET 필름 중 하나는 polydimethylsiloxane (PDMS)가 코팅된 PET 필름이다. PDMS가 코팅된 PET 필름은 릴리스 라이너로서 optically clear adhesive (OCA), 웨이퍼, 평면 디스플레이, 인쇄회로기판 등의 표면을 보호하는데 많이 사용된다. 그러나 PDMS가 코팅된 PET 필름은 PDMS 층을 PET 필름으로부터 제거하지 않으면 재활용하기 어렵다. 따라서, PDMS 층을 제거하기 위해 팽윤시키고 물리적으로 떼어내는 전처리 공정을 연구하였다. 전처리 결과, PET 필름에 남아있는 PDMS 코팅의 양은 전체 PDMS 양의 1%까지 감소하였다. 전처리한 필름을 글리콜리시스한 결과, bis(2-hydroxyethyl terephthalate) (BHET)를 85.24%의 수율로 얻었다. 이 전처리는 PDMS가 코팅된 PET 필름을 재활용 가능하게 할 것이다.