The present study investigates the role of Al in the evolution of the crystalline phases of an alkali-activated binder. Samples were synthesized corresponding to the binder composition with various $Al_2O_3/Na_2O$ and MgO/binder ratios in hydrothermal condition. Thermodynamic modelling was carried out to predict the effect of the Al content in the binder composition on the formation of Al-bearing phases. The test results showed that an increasing Al content led to the alteration of the predominant zeolitic crystalline phase in the alkali-activated binder. In addition, MgO incorporation enhanced the reaction degree of hydration in the alkali-activated system and the crystal growth, specifically hydrotalcite-like phase. Consequently, the formed reaction products had a great effect on the pore characteristics of the alkali-activated binder given their variations in the crystal structure.
본 연구는 알루미늄이 수열합성조건에서 알칼리 활성 바인더의 결정상 형성에 미치는 영향을 조사하였다. 샘플은 다양한 $Al_2O_3/Na_2O$, MgO/binder비에 따라 수열합성조건에서 합성되었다. 실험결과, 바인더 조성비에서 Al 함량의 증가는 생성되는 주요 제올라이트 계 결정상의 변화를 초래하였다. 또한, MgO의 첨가는 알칼리 활성 반응에서 수화반응도를 향상시켰으며, 하이드로탈사이트 계 결정상의 형성을 증가시켰다. 이러한 반응생성물은 각기 다른 결정구조를 가짐으로써 알칼리 활성 바인더의 공극 특성에 중요한 영향을 미치는 것으로 확인되었다.