The transparent electrode film is a thin film layer composed of optically transparent and conductive material, and is applied to various applications such as organic light emitting diodes, wearable devices, and touch screens. At present, metal oxides such as indium tin oxide (ITO) are widely used as materials for transparent electrode films, but they are disadvantageous in that they are expensive and are not flexible enough to be used in applications where flexible elements or mechanical shocks are continuously received. Therefore, copper nanowires that are flexible and have low process costs as next-generation materials are being studied. However, copper nanowires have low resistance to oxidation, so that the network between wires and wires is not well formed, resulting in deterioration of electrical and optical characteristics and poor durability. In this paper, we have conducted research to improve the electrical and optical properties of copper nanowires to a level that can be commercialized by completely removing the oxide layer formed on the surface of the copper nanowires by a post - treatment method using acetic acid and forming a smooth network. In addition, a transparent electrode film having excellent oxidation resistance has been developed by synthesizing a thin and uniform silver shell on the surface of the copper nanowire.
투명전극필름은 광학적으로 투명하면서 전도성을 지닌 물질로 구성된 박막 층으로, 유기발광 다이오드, 웨어러블 소자, 터치 스크린 등의 다양한 어플리케이션에 응용되고 있다. 현재에는 투명전극필름의 소재로 인듐주석산화물(ITO)와 같은 금속산화물이 널리 사용되고 있으나, 가격이 비싸고 소재가 유연하지 못해 유연성 소자나 기계적인 충격을 지속적으로 받는 응용분야에 사용하기 어려운 단점이 있다. 따라서 이를 대체하기 위해 유연성이 좋고 공정 비용이 저렴한 구리 나노와이어가 차세대 소재로써 연구되고 있다. 그러나 구리 나노와이어는 산화 저항성이 낮기 때문에 와이어-와이어 간의 네트워크가 잘 형성되지 않아 전기적, 광학적 특성이 저하되고, 내구성이 안 좋은 단점을 가지고 있다. 따라서 본 연구논문에서는 아세트산을 이용한 후-처리 방법을 통해서 구리 나노와이어 표면에 형성된 산화 층을 완전히 제거하고 원활한 네트워크를 형성시켜 상용화 가능한 정도의 전기적, 광학적 특성을 개선시키는 연구를 진행하였으며, 구리 나노와이어의 표면에 얇고 균일한 두께의 은 층을 형성하는 합성법을 개발하여 산화 저항성이 우수한 투명전극필름을 개발하였다.