The effects of Cr and Al on the Co-Ti-W alloys with respect to atomic partitioning tendency and high-temperature properties of Co-Ti-W-based alloys containing $\gamma$/$\gamma$' phases were observed. Cr additions to a Co-Ti-W base alloy caused a decrease in $\gamma$' volume fraction, while additions of Al caused substantially increases of $\gamma$' volume fractions. These alloy designs resulted in decreased lattice misfits of $\gamma$/$\gamma$' phases. Ti and W partitioned to the $\gamma$' phase, while Co, Cr, and Al partitioned to $\gamma$ confirmed by APT. Thermal property, mechanical property, and oxidation resistance of the alloys were also measured. The thermal stability of the $\gamma$' phase increased with the addition of Cr and Al and the yield stress changed greatly at high temperatures. However, the added amount of Cr and Al was small and the increased resistance to oxidation was not identified.
Co-Ti-W을 기반으로 한 합금에 Cr과 Al을 첨가하여 미세구조 및 원자들의 거동 변화와 고온 특성을 관찰했다. Co-Ti-W 합금에 Cr을 첨가하면 $\gamma$'의 상분율이 감소하였고, 첨가된 Al은 $\gamma$'의 상분율을 크게 증가시켰다. 이러한 합금 설계는 $\gamma$/$\gamma$'의 격자 상수 불일치를 감소시켰다. 원자 탐침 단층 촬영(Atom probe tomography, APT)법을 이용하여 Ti과 W은 $\gamma$' 상으로, Co와 Cr, Al은 $\gamma$ 상으로 편석하는 것을 확인했다 또한 재료의 열적 특성, 기계적 특성, 그리고 산화 저항성을 측정했다. Cr, Al을 첨가하자 $\gamma$'상의 열적 안정성이 증가하였고 고온에서 항복 응력이 크게 변하였다. 반면에 첨가한 Cr, Al의 적은 함량으로 인해 산화 저항성의 증가는 확인 되지 않았다.