The present study investigated the physicochemical characteristics of alkali-activated fly ash/slag (AAFS) modified by MgO and the influence of MgO on the chloride penetration resistance of AAFS. MgO was added to replace the fly ash and slag at dosages of 0%, 5% and 10% by weight of the binder. Samples were immersed in a 10 wt% sodium chloride solution for 91 days. The results showed that the formation of hydrotalcite was promoted by MgO incorporation. Hydrotalcite was found to be effective in improving chloride penetration resistance. However, there exists a threshold level upon which the amount of hydrotalcite may not further increase the chloride penetration resistance. In addition, the adsorption of chloride in AAFS can be seen not only as the result of effects of hydrotalcite but also as the combined effect of the pore network structure and pore solution chemistry.
본 연구는 산화마그네슘을 혼입한 알칼리활성 플라이애시/슬래그의 물리화학적 특성과 알칼리활성 플라이애시/슬래그의 염화물 침투 특성에 대한 산화마그네슘의 영향을 조사하였다. 산화마그네슘은 플라이애시와 슬래그를 대체하여 결합재 무게 대비 0%, 5%, 10%로 첨가되었다. 시편들은 10% 농도의 염화나트륨 용액에 91 일동안 노출되었다. 실험결과는 하이드로탈사이트의 생성이 산화마그네슘에의 첨가에 의해 촉진됨을 보여주었다. 하이드로탈사이트는 염화물 침투 저항성을 향상시키는데 효과적이라는 것을 밝혀내었다. 하지만, 하이드로탈사이트의 양이 염화물 침투 저항성을 더 이상 증가시키지 않을 수 있는 임계점이 존재하였다. 또한, 알칼리활성화 플라이애시/슬래그의 염화물 흡착은 하이드로탈사이트의 효과뿐만 아니라 공극 네트워크 구조와 공극 용액의 화학적 성질이 결합된 효과의 결과로 볼 수 있다.