In this thesis, nickel oxide and znic oxide nanoparticles which has used in multilayer optoelectronic device with excellent optical and electrical properties are mainly discussed. In the case of nickel oxide, it was co-doped with copper ions having different oxidation numbers of copper (I) and copper (II). The enhancement of conduction / injection was confirmed by electrical analysis and it was determined that the improvement of electrical properties were result of chemical composition change by chemical analysis. The co-doped nickel oxide film adjusted OLED showed 1.5 times increased current efficiency compared to the conventional nickel oxide device by improving the charge balance. Zinc oxide was hybrided with two multifunctional polymers. Optical and chemical analysis indicated the surface defect passivation and observed the shift in injection barrier due to the interface dipole effect. The vinyl and methyl backbones of the polymers improved the charge balance by suppressing the excessive electron current in the Cd-based QLED and QLED showed the current efficiency of 34.7 Cd/A.
본 학위논문에서는 뛰어난 광학적 특성, 전기적 특성 등을 바탕으로 다층구조 광전자 소자에 사용되는 산화 니켈, 아연 나노입자에 대해 주로 다루었다. 산화 니켈의 경우 구리(I)와 구리(II)의 다른 산화수를 가지는 구리 이온들로 혼재 도핑 되었다. 전기적 분석을 통해 전도/주입 능력의 향상을 확인하였고 화학적 분석으로 전기적 특성의 변화가 화학적 결합 변화에 의한 것을 확인 하였다. 이 필름이 적용된 OLED는 전하 균형이 개선되어 기존 니켈 산화물 소자 대비 1.5배의 발광 효율을 보였다. 산화 아연은 두가지 다기능성 고분자와 혼합되어 비교되었다. 광학적, 화학적 분석을 통해 표면 결함 개질 여부를 확인 하였고 계면 쌍극자 효과에 의한 주입 장벽 변화를 관찰하였다. 고분자들의 메틸기와 바이닐기 뼈대는 카드뮴 계열의 QLED에서의 과도한 전자 전류를 억제시켜 전하 균형을 개선시켰고 최대 34.7 Cd/A의 효율을 보였다.