A new type of conjugated ionic polyacetylene was synthesized by metathesis polymerization of betaine monomers, alkyl dipropargyl (4-sulfobutyl) ammonium betaines(ADPSAB). The polymerization of ADPSAB was carried out with various transition metal catalyst systems. The $MoCl_5$ and $PdCl_2$ were found to be a particularly effective catalyst for the cyclopolymerization of the betaine monomers.
FT-IR, $^1H$ NMR, $^{13}C$ NMR and UV-visible spectroscopies showed that poly(ADPSAB) possess polyene structure having cyclic recurring units in the polymer backbone. Unlike polyelectrolyte, the resulting polymers were more soluble and showed higher viscosities in the salt than in salt-free solution (antipolyelectrolytes).
When doped with an accepter such as iodine, the polymers exhibited a substantial increase($\sim10^{-3}S/cm$) in electrical conductivity compared to the undoped state($\sim10^{-10}S/cm$).
새로운 베타인 형태의 공액 이온성 폴리아세틸렌이 전이금속 촉매를 이용한 메타세시스 중합에 의하여 합성되었다. 사용된 모노머는 알킬기로 에틸, 부틸, 헥실, 그리고 옥틸기를 가지는 알킬디프로파길-4-술포부틸 암모늄베타인이며, 이러한 베타인 모노머의 고리화중합은 $PdCl_2$촉매에서 가장 좋은 촉매활성을 보였다. 알킬사슬이 긴 옥틸이나 헥실사슬의 경우 $MoCl_5$ 단독촉매에서도 효과적으로 중합이 진행되었다.
합성된 폴리머들은 $^1H$, $^{13}C$ NMR, FT-IR, UV-visible과 같은 분광학적 방법에 의해 중합체의 주사슬이 공액 이중결합과 주로 6각형의 고리를 포함하는 구조를 갖는 것으로 확인되었으며, UV 흡수파장으로부터 합성된 중합체들 은 10~14 정도의 공액길이를 가지는 것을 알 수 있다.
얻어진 폴리머는 수소를 가지는 극성 유기용매나 불소가 치환된 알코올, 술폰이온과 수소결합을 할 수 있는 강산에 좋은 용해도를 보였다. 합성된 폴리머들은 곁사슬의 베타인 형태에 기인한 특이한 용액특성을 보이는데 이것은 폴리베타인의 안티폴리일렉트롤라이트한 성질로 동일한 고분자 농도의 용액상태에서 염 (NaBr)을 첨가함에 따라 측정되는 점성도가 증가하는 것이다. X-선 회절분석에 의해 중합체가 비결정성을 가지는 것을 확인할 수 있었다. 전기전도도는 물리적 특성이 좋은 PVA와 합성된 폴리머를 용액상에서 블렌드하여 측정하였으며, 요오드로 도핑한 중합체들의 전기전도도는 $\sim10^{-3}S/cm$로 나타났다.