Excess tritium analysis was performed to verify whether or not cold fusion occurs during electrolysis of heavy water in the current density range of 83~600 mA/㎠ for a period of 24~48 hours with use of palladium electrodes of 7 different processing treatments and geometries. The extent of recombination of $D_2$ and $O_2$ gases in the electrolytic cell that must be taken account in the calculation of accurate enthalpy values was also examined. The behavior and interaction of hydrogen atoms with defects in Pd electrodes were examined using the Sieverts gas charging and the positron annihilation(PA) method.
Tritium enrichment was observed during electrolysis but excess tritium that could be considered as a by-product of cold fusion was not detected under the present electrolysis conditions. The extent of recombination of $D_2$ and $O_2$ gases was 32%. Hence the excess heat could be generated due to exothermic reaction of recombination but not due to nuclear fusion.
Lifetime results from the PA measurements of the Pd electrodes indicated that hydrogen atoms could be trapped at dislocations and vacancies in the electrodes and that dislocations were slightly more perferred sites than vacancies. R parameters from the PA measurements of the hydrogen-charged Pd electrodes indicated that the formation of hrdrides was accompanied by generation of mostly dislocations. Doppler broadening results of the Pd electrodes indicated that lattice defect sites where positrons were trapped were increasing followed by decreasing repetitiously as electrolysis continued. PA measurements of the cold-rolled Pd and the Pd hydride specimens annealed isochronally indicated that microvoid-type defects existed in the hydrogen-charged electrode specimen.
상온핵융합의 실험적 검증을 위하여 가공조건 및 기하학적조건이 다른 7 종류의 팔라디움전극을 사용하여 24~48 시간, 전류밀도 83~600 mA/㎠ 의 조건으로 전기분해를 실시하였다. 상기조건하에서 삼중수소의 농축에 기인한 분리팩타 (separation factor)를 측정하였고 핵융합의 부산물인 삼중수소증가량을 측정하였다. 또한 초과열 계산과 관련된 K(net Faradic efficiency)를 측정하여 산소/중수소 가스의 재결합정도를 조사하였다. 양전자소멸측정장치 및 일정체적 가스주입장치를 이용하여 팔라디움전극에서 격자결함과 중수소 (수소)의 반응 및 거동현상에 대하여 조사되어졌다.
전기분해하는동안 삼중수소 농축현상이 관찰되었고 핵융합의 증거가 될 만한 삼중수소양은 검출되지 않았다. 한편 산소/수소 가스의 재결합 정도는 32% 로 나타났다. 이는 재결합과정이 발열반응이므로 전기분해과정에서 핵반응과 관계없이 초과엔탈피가 발생할수 있음을 의미한다. 양 전자소멸측정장치를 이용하여 양전자수명, 양전자소멸밀도, P/W 및 R 파라메터의 측정을 통하여 전극의 격자결함 (전위 및 공공)에 수소가 집적 (trap)되며 수소집적은 공공에서보다 전위에 약간 더 선호하는 것으로 나타났다. 전극의 수소화물형성에 기인하여 대부분 전위의 발생을 나타냈다. 또한 팔라디움수소화물의 등시소둔실험을 통하여 소량의 미소공동 형태의 결함의 존재를 나타내었고 그 결함의 크기는 수 Å정도로 조사되었다.