High $T_c$ superconductors of $Y_1Ba_2Cu_3O_{7-x} and Bi(Pb)SrCaCuO were prepared by solid state reaction method. These samples are examined for AC susceptibility and Harmonics under several conditions with varying temperatures; AC and DC magnetic intensity, and frequencies.
About 0.4-0.8K upshift in $T_c$ for high frequency (1MHz) in case of AC magnetic susceptibility measurement are all observed. Two steps transition is observed for Bi-system, the first transition is sensitive to frequency, but second transition is sensitive to AC and DC magnetic field. From the peak temperatures of x' of AC susceptibility for AC magnetic intensity are obtained and magnetic response for two samples compared. We observed clearly all odd harmonics in the Harmonics measurement, up to at least n=7 for Y-system and n=31 for Bi-system. The results suggest that high $T_c$ superconductor is composed of grains, and these grains are connected by Josephson junction. The nonlinear properties due to superconducting transition was observed from second harmonics under DC magnetic fields and with temperatures.
고온 초전도체의 자기적인 특성을 조사하기 위하여 $Y_1Ba_2Cu_3O_{7-x}$와 Bi(Pb)SrCaCuO계를 고상 반응법으로 제작 하였고, 이들의 교류 자화율및 고조파를 직류 자기장의 세기, 교류 자기장의 세기 및 진동수에 대하여 온도를 변화시키면서 그 특성을 조사하였다.
교류 자화율 측정의 경우에서는 두 시료 모두 고진동수 (1MHz)에서 $T_c$ (critical temperature)가 약 0.4-0.8K 상승한 것을 관측하였다. 특히 Bi-계에서는 뚜렷한 두 단계의 전이가 일어나는데, 첫번째 단계의 전이는 진동수에 민감한 반면에 두번째 단계의 전이는 자기장의 세기에 민감한 부분인 것을 알았다. 또한 자기장의 세기에 따른 교류 자화율의 imaginary part의 peak temperature 변화로써 두시료의자기적인 성질을 비교하였다.
고조파의 측정을 통하여 $Y_1Ba_2Cu_3O_{7-x}$ 시료에서는 n=7, Bi(Pb)SrCaCuO계 시료에서는 n=31 의 고조파를 쉽게 관측할 수 있었다. 이들 실험 결과는 초전도체의 grain들이 Josephson junction으로 연결되어 있다는 것을 알 수 있었다. 즉 이들 시료의 granular 특성을 관측할 수 있었다.