Interpolymer complex formation between PLP with helical structure and PMAA with random coil structure through hydrogen bonding has been studied by several experimental techniques e.g., viscosity, turbidity, and pH measurements. The change of pH as a function of time shows that the interpolymer complex formation follows the second order reaction first and then deviating toward first order in the final stage of reaction. It is consistent with the general pathway of interpolymer complex formation, i.e., nucleation followed by chain growing. The viscosity, turbidity, and pH experiments show that the left-handed helix of PLP (Form Ⅱ) forms complex with PMAA faster than the right-handed helix of PLP (Form Ⅰ). The expectation of the high ability of the left-handed helix of PLP from the geometrical and structural point of view is agreeable to the experimental results. From the turbidity and pH measurements, unexpected results were found out such as the high ability of complexation at intermediate PLP conformer (θ=45) which coexists trans-cis monomers equally and the pH fluctuation deviating from the regular trend. The high ability of complexation at intermediate PLP conformer (θ=45) may be caused by the high flexibility of the intermediate PLP conformer since several kink in helix may make the helix flexible and partly disordered state. The pH fluctuation showed the irregular feature corresponding to the trans fraction of PLP. It may be the result of reversible process between intermediate steps. The existence of kink and the mechanism of complexation must be investigated further.
Helical 구조의 PLP와 random coil 구조를 갖는 PMAA의 수소결합에의한 고분자 중합체 형성을 점도, 흐림도, 산도등의 방법을 이용하여 연구하였다. 시간에 따른 산도의 변화 실험에서 고분자 중합체 형성은 2차 반응의 특징을 갖다가 반응이 지남에 따라 1차 반응으로 옮겨감을 알 수 있었다. 이러한 사실은 고분자 중합체 형성이 우선 핵을 만들고 이곳에서부터 고분자 중합체가 형성됨을 의미하는 것이다. 산도와 흐림도의 실험에서 PMAA는 PLP Form Ⅰ (right-handed helix)보다 PLP Form Ⅱ (left-handed helix)와 고분자 중합체를 더 잘 형성함을 알수있었으며 이는 PLP의 두 helices의 구조적 성질의 차이에서 기인함을 알 수 있었다. 또한 이 실험에서 Form Ⅰ 과 Form Ⅱ 가 균등히 섞여있는 PLP 중간체 (θ=45)는 PMAA와 매우 뛰어난 중합체 형성 능력을 보였으며 이러한 결과는 PLP 중간체가 중합체 형성 능력이 큰 구조를 갖는다는 것을 의미한다.
결론적으로 PLP의 구조는 고분자 중합체 형성의 과정과 결과에 커다란 영향을 미친다는 사실을 알 수 있었으며, PLP의 구조적 변이에서 PLP 중간체 (θ=45)는 중합체 형성 능력이 뛰어난 구조를 갖는다는 새로운 사실을 발견하였다.