As [M]/[I] ratios increase at constant coinitiator concentration, the reaction reached nearly complete conversion and the number average molecular weight passed a maximum. It was observed that for constant initiator concentration the maximum conversion with increasing coinitiator concentration was showed. The molecular weight and dispersity by GTP of methacrylate (MA), n-butyl methacrylate(BMA), acrylonitrile(AN), 2-(trimethylsilyoxy) ethyl methacrylate, and methylmethacrylate(MMA) in tetrahydofuran (THF) or N,N-dimethylformamide (DMF) as solvent with hexamethyldisilazane (HMDSZ) as initiator and tetrabutylammonium fluoride (TBAF) as coinitiator were obtained in the range $\underline{6300}$ to $\underline{23600}$ and $\underline{1.05}$ to $\underline{7.41}$, respectively.
Block copolymers, e.g., PMMA/PBMA, PMMA/PBMA, PMMA/PHEMA, PBMA/PHEMA, and PMMA/PAN were synthesized by GTP. It will be investigated that the process of this polymerization can also be used to prepare polymers containing one or more specially located functional groups.
일정한 조개시제 농도에서 모노머 대 개시제 비가 증가함에따라 반응은 정량적으로 진행되었고, 수평균분자량은 증가했다. 그리고 일정한 개시제 농도에 대해 조개제의 농도가 증가함으로써 수율이 증가함을 보였다. 용매로는 테트라히드로푸란 또는 N, N-디메틸포름아미드에서 개시제로 헥사메틸딜살라잔과 조개시제로 테트라부틸암모늄 불소이온으로 메타아크릴레이트, 부틸메타아크릴레이트, 아크릴로니트릴, 2 - (트리메틸실릴옥시) 에틸 메타아크릴레이트와 특히 메틸메타아크릴레이트의 이동기 중합에 의한 분자량과 dispersity 가 반응조건에따라 6300 - 23600 과 1.05 - 7.41 의 분포를 나타냈다.
이동기 중합방법으로 PMMA/PBMA , PMMA/PBMA , PMMA / PHEMA , PBMA / PHMA, 그리고 PMMA / PAN 의 블록 공중합체를 합성했다.
이런 중합과정에 대해 하나 또는 두개이상 치환된 작용기들을 포함하는 중합체를 합성할 것이다.