Zircaloy-4 의 요드유기 응력부식파괴에 대한 미세조직의 영향에 관한 연구 = A study on the effects of microstructure on the iodine-induced stress corrosion cracking of zircaloy-4
서명 / 저자 Zircaloy-4 의 요드유기 응력부식파괴에 대한 미세조직의 영향에 관한 연구 = A study on the effects of microstructure on the iodine-induced stress corrosion cracking of zircaloy-4 / 김재익.
저자명 김재익 ; Kim, Jae-Ik
발행사항 [서울 : 한국과학기술원, 1986].
Online Access 제한공개(로그인 후 원문보기 가능)원문

소장정보

등록번호

4104052

소장위치/청구기호

학술문화관(문화관) 보존서고

MMS 8641

휴대폰 전송

도서상태

이용가능

대출가능

반납예정일

리뷰정보

초록정보

The effects of microstructure on iodine-induced stress corrosion cracking(ISCC) of Zircaloy-4 tube was studied by an internal pressurization test method at temperature 330℃ and at iodine concentration of 2.2 mg/㎠. The threshold stress was found to be 400 MPa for stress - relieved, 350 MPa for water quenched and for 280 MPa air cooled Zircaloy-4 tube respectively. The following relationship was found between the failure time ( $t_f$ ) and hoop stress ( ${\sigma}_n$ ) at the stress of threshold level : $t \propto exp(-C{\sigma}_n)$ In the above equation the values of constant C were found as follows C = 0.046 for stress-relieved Zircaloy-4 C = 0.022 for water quenched Zircaloy-4 C = 0.012 for air cooled Zircaloy-4 It was found that the SCC resistivity exhibit minimum value at a certain strain rate of 1-6×10$sec^{-6}$.

서지기타정보

서지기타정보
청구기호 {MMS 8641
형태사항 [iii], 59 p. : 삽도 ; 26 cm
언어 한국어
일반주기 저자명의 영문표기 : Jae-Ik Kim
지도교수의 한글표기 : 박진영
지도교수의 영문표기 : Jin-Young Park
학위논문 학위논문(석사) - 한국과학기술원 : 재료공학과,
서지주기 참고문헌 : p. 27-30
주제 Stress corrosion.
Fractures.
Microstructure.
응력 부식. --과학기술용어시소러스
파괴. --과학기술용어시소러스
미세 조직. --과학기술용어시소러스
Strain rate.
QR CODE qr code