Complex formations between syndiotactic poly(methacrylic acid) (st-PMAA) and poly(N-vinyl pyrrolidone) (PVP), and that between st-PMAA and polyethyleneoxide (PEO) through hydrogen bonding were studied by viscosity and potentiometry. Reduced viscosity ($\eta_{red}$) was measured at various mole fraction of PVP or PEO with respect to a constant amount of st-PMAA. Observation shows a sharp minimum at the 1:1 mole ratio of st-PMAA : PVP or st-PMAA : PEO, which shows that the complexation becomes optimal and the complex has a compact structure in this case. Variation of pH also supports this conclusion. This is the case of the system of st-PMAA and PVP in water as well as in DMF. Also the complexation is much enhanced when the molecular weight of PVP is high. Meanwhile, the system of st-PMAA and PEO shows a little different behavior, i.e., this system does not form the complex in DMF and dose only in water. It is because the interaction st-PMAA with PEO is weaker than that with PVP.
신디오탁틱 폴리 메타크릴산(st-PMAA)과 폴리비닐피롤리돈(PVP) 또는 폴리에틸렌옥사이드(PEO)와의 복합체 형성을 물과 디메틸포름아마이드(DMF)하에서 점성도법과 전위차법에 의해 연구하였다.
환산점성도$(\eta_{rel})$는 PVP와 PEO의 몰분율의 변화에 따라 측정하였다. 이 경우 st-PMAA와 PVP 또는 PEO와의 몰비가 대략 1:1인 경우에 환산점성도가 최하점에 도달하게 된다. 이것은 복합체 형성이 이 경우 에 가장 잘 이루어지며, 가장 밀집된 형태의 구조를 가지게 됨을 알 수 있다. pH의 변화도 같은 결과를 나타내고 있다. 여기서 st-PMAA와 PVP는 물 뿐만 아니라 DMF하에서도 복합체가 잘 형성된다. 그러나 PEO의 경우 물에서는 복합체가 잘 형성되지만 DMF하에서는 형성되지 않는다. 이것은 PVP가 PEO보다는 산과의 수소결합능력이 강하다는 것을 알 수 있다. 또한 PVP의 경우 분자량이 클수록 복합체 형성이 잘 되고 있음을 알 수 있다.