The Barkhausen noise and its ringdown counts and peak amplitude distribution have been studied during magnetization cycle in polycrystalline sheets of 78% Ni-Fe and 3% Si-Fe.
The Barkhausen noise was predominantly observed on the steepest part of hysteresis loop and the RMS voltage of the noise decreased as the samples were annealed. This result is supposed to be caused by the removal of residual stress and texture in the annealed samples.
The ringdown counts and peak amplitude distribution as well as RMS voltage decreased with increasing magnetizing frequency. It is concluded that ringdown counts and peak amplitude distribution are adequate parameters for exploitation of Barkhausen noise.
다 결정체 78.5% Ni-Fe 및 3% Si-Fe 평판에서 자기 이력곡선의 각 특이점에 해당하는 Barkhausen noise 의 파형을 관찰하고 mean amplitude를 측정하였으며 자화 frequency 가 이것에 미치는 영향을 조사하였다. 실험결과 Barkhausen noise 의 amplitude 는 자기이력곡선상의 미분 변화율 변화가 급격한 곳에서 최대였으며 열처리한 시편에서는 줄었다. 새로운 시도로 AE 에 사용되는 parameter 인 ringdown counts와 peak amplitude distribution 으로 Barkhausen noise의 신호분석을 한 결과 이들은 Barkhausen noise 해석에 적합한 parameter 임을 알 수 있었다.