The density and percentage crystallinity of glass ceramic (BOS-1 System) was increased with heat treatment time and the crystalline phase was identified as alumina diopside.
Ultrasonic attenuation measurement with 5MHz longitudinal wave showed exponential dependence on the percentage crystallinity, then acoustic emission response in total counts during hardness indentation varied exponential dependence on $(Hv)^{-\frac{1}{2}}$. The variation would be caused by interdependence between the work done by the indentor and the diagonal of indentation.
Ultrasonic attenuation, α in Nepers/cm, and acoustic emission response, ∑N in total counts, in glass ceramic is expressed as $(ℓn g(\displaystyle\sumN))^2(ℓn hα) = K$ where constants g, h and k are 7259, 7.92 and 234, respectively. This implies that when the source energy during indentation is released through its medium, acoustic emission response is determined by ultrasonic attenuation which controlled by the energy loss propagating through medium.
Glass ceramic (BOS-1계)의 밀도와 결정도는 열처리 시간에 의하여 증가하고 그리고 결정은 alumina diopside 임이 밝혀졌다.
5MHZ 종파로 초음파 감쇄 측정은 결정도에 지수적으로 의존함을 보여주고, 강도 측정시 총 수로써 acoustic emission 반응은 $(Hv)^{-\frac{1}{2}$} 지수적으로 의존하여 변화한다. 이 변화는 들어간 부분의 대각선과 indentor에 의하여 하여진 일과 서로 의존함으로 생긴다.
Glass ceramic 에서 초음파 감쇄 α (Nepers/cm)와 acoustic emission 반응 ∑N (총수)는 $(ln g(\displaystyle\sumN))^2(ln hα) = k$로 나타내어지고, 이때 g, h, k는 7259, 7.92, 234이다. 이것은 감도측정시원천 에너지가 매질을 통해 방출될 때, 매질을 통하여 전파하는 파의 에너지 감소에 의하여 결정되는 초음파 감쇄에 의하여 acoustic emission 반응이 결정되어진다.