Ethylene oxidation was investigated in a pulse type reactor over silver catalysts supported by $α-Al_2O_3$ and $SnO_2$. $Ag/α-Al_2O_3$ catalysts showed greater activity and selectivity than Ag/$SnO_2$ catalysts. Both $Ag/α-Al_2O_3$ and Ag/$SoO_2$ catalysts showed maximum activity at 5.66 Wt % silver content. As the silver content increased in the region that showed optimum activity, the selectivity for ethylene oxide formation increased on Ag/$α-Al_2O_3$ catalysts whereas the selectivity decreased on Ag/$SnO_2$ catalysts. Increase in the reaction temperature resulted in a decrease in the selectivity for ethylene oxide formation. The decrease in the selectivity was more pronounced for Ag/$SnO_2$ catalyst than $Ag/α-Al_2O_3$ catalyst. EPR spectra of oxygen adsorbed on $SnO_2$ showed a symmetric signal with g=2.002 when oxygen was adsorbed above 200℃. The signal was assigned to O species. Decrease in the selectivity of ethylene formation was interpreted in terms of a participation of $O^-$ species in the reaction that leads to a formation of complete oxidation products $CO_2$ and $H_2O$.
$α-Al_2O_3$와 $SnO_2$에 의해 담지된 은촉매상에서의 etylene 산화반응을 살펴보았다. 생성물로서 이산화탄소, 물, etylene oxide가 생성되었다.
$Ag/α-Al_2O_3$ 촉매는 $Ag/SnO_2$ 촉매보다 나은 활성과 선택성을 보였다. 이 촉매들은 5.66Wt%에서 최대 활성을 보였으며 촉매에서의 은의 함량이 증가함에 따라 $Ag/α-Al_2O_3$에서는 ethylene oxide 생성의 선택성이 증가하나 $Ag/SnO_2$에서는 반대의 현상이 나타났다.
반응온도가 올라감에 따라 선택성이 감소하는데 이는 $Ag/SnO_2$ 촉매들이 $Ag/α-Al_2O_3$ 촉매보다 더 심하였다. 각 촉매들의 은함량변화에 따른 Auger spectra의 변화를 관측하여 촉매 표면에 서의 은입자가 성장함을 알 수 있었다. $SnO_2$의 EPR실험에서 200℃ 이상의 온도에서 산소가 흡착 하였을 때 표면에 흡착된 $O^-$와 관계된 hole이라 생각되는 g=2.002의 signal을 얻었다. 이와같은 현상에서 ethylene 산화반응은 담체의 특성과 은입자의 크기와 형태에 크게 의존하며 $SnO_2$ 표면의 $O^-$가 반응에 참여함을 추론할 수 있었다.