Stress aging treatment was conducted at various treatment conditions for three Cu-Zn alloys ; cold rolled 65:35 brass (BsS2A-H), annealed free cutting brass (MBsBD2A) and annealed 70:30 brass (BsBD1).
The effect of treatment stress, temperature and time that control the stress aging reactions was studied and the change in mechanical properties and electrical conductivity after treatment studied.
Strain aging (for cold rolled material) and plain aging (for annealed materials) were also conducted to compare the results with those of stress aging treatment.
It was found that stress aging treatment has increased the proportional limit remarkably for the alloys treated. In case of free cutting brass (MBsBD2A), 0.2% offset yield stress was increased markedly.
Micromechanisms that govern the stress aging reactions were also discussed for each alloy.
Optical and electron microscopic studies were attempted for the cold rolled 65:35 brass (BsS2A-H).
냉간 압연된 65:35 황동, 풀림 처리된 쾌삭 황동 및 풀림 처리 된 70:30 황동 등 세가지 구리 - 아연 합금에 대하여 여러가지 조건 하에서 응력 시효 처리를 하였다.
응력 시효 처리에 있어서 응력, 처리 온도 및 처리 시간이 미치는 영향과 처리후 기계적 성질 및 전기 전도도의 변화를 고찰 하였다.
변형시효 (냉간 압연된 재료에 대하여) 및 단순 시효 (풀림 처리한 재료에 대하여) 처리에 대한 실험도 실시 하였으며 응력 시효처리 결과와 비교 하였다.
응력 시효 처리를 한 결과 세가지 재료 모두 다 비례 한도가 크게 상승 하였으며 쾌삭 황동의 경우에는 항복 응력도 현저히 증가 하였다.
각 재료에 있어서 응력 시효 현상을 일으키는 미세 기구에 관하여도 고찰 하였으며 냉간 압연된 65:35 황동에 대해서는 광학 및 전자 현미경을 이용하여 조직 변화를 관찰 하였다.