Analysis of anisotropy in high modulus and high strength Carbon/Epoxy laminae and laminates has been made under the same testing conditions.
For high modulus Carbon/Epoxy laminae, modulus measurement showed that tensile moduli were 25% greater and 14% less than compressive moduli for (0˚) and (90˚) respectively.
For high strength Carbon/Epoxy laminae, modulus measurement showed that tensile moduli were 31% greater and 7% less than compressive moduli for (0˚) and (90˚) respectively.
Comparison of theoretical prediction and experimental result of the location of neutral axes for high strength Carbon/Epoxy laminates showed a fairly good agreement except (90˚/0˚) and (90˚/0˚/90˚) laminates where (90˚/0˚) lamina was subjected to compressive load.
본 실험에서는 High Modulus 탄소섬유와 고강도 탄소섬유가 사용되었다. High Modulus 단층판의 인장실험과 굽힘실험 결과 (0˚) 단층판에서는 인장 Modulus 가 압축 Modulus 보다 25%정도 더 컸고 (90˚) 단층판에서는 14%더 작았다.
고강도 탄소섬유 단층판 실험결과 (0˚) 단층판에서는 인장 Modulus 가 압축 Modulus 보다 31%더 컸고 (90˚) 단층판에서는 7%더 작았다. High Modulus 단층보의 굽힘실험 결과 4점 굽힘실험시의 굴곡강도가 3점 굽힘실험에서의 굴곡강도보다 약 20%정도 더 큰 것을 알수 있었는데 이것은 3점 굽힘실험시 하중점에서의 응력집중이 4점 굽힘실험에서의 그것보다 더 크다는 것을 의미한다.
여러가지 적층 배열을 갖는 고강도 탄소섬유 적층보의 4점 굽힘실험에서는 이론와 실험치가 대체로 일치하였으나 (90˚) 단층판이 압축하중을 받는 (90˚/0˚) 와 (90˚/0˚/90˚) 적층보 실험에서는 이론치와 실험치의 편차가 비교적 크게 나왔다.