Phenylphosphonyl-N,N'-bis-ε-Caprolactam/KOH 촉매에 의한 2-Pyrrolidone 의 음이온 중합 = Anionic polymerization of 2-pyrrolidone via phenylphosphonyl-N,N'-bis-ε-caprolactam/KOH

• 서명 / 저자: Phenylphosphonyl-N,N'-bis-ε-Caprolactam/KOH 촉매에 의한 2-Pyrrolidone 의 음이온 중합 = Anionic polymerization of 2-pyrrolidone via phenylphosphonyl-N,N'-bis-ε-caprolactam/KOH, 자유 라디칼 Telomerization 에 의한 스티렌-메타크릴산 메틸 block 혼성중합체의 합성 및 분석 = Synthesis and characterization of poly(styrene-b-methyl methacrylate)by free radical telomerization / 박정학.
• 발행사항: [서울 : 한국과학기술원, 1980].

Anionic polymerization of 2-pyrrolidone was carried out with PPBC/KOH catalysis. The effects of PPBC/KOH mole ratio, KOH concentration and temperature on polymerization were investigated. It was observed that the highest rate of polymerization and maximum conversion were obtained when PPBC/KOH mole ratio was around 0.5. The maximum conversion and the highest viscosity were obtained when the concentration of KOH was 2 mole percent. It was also observed that while the rate of polymerization at 50℃ was higher than at 30℃ in the initial stage of polymerization, the conversion and viscosity decreased as polymerization time was extended. The rate of polymerization was determined by least square method.

PPBC/KOH 촉매작용을 이용한 2-pyrrolidono의 음이온중합에 있어서 PPBC/KOH 몰 비, KOH의 농도 및 온도가 중합에 미치는 영향을 조사하였다.
PPBC/KOH 몰 비가 0.5일 때 중합속도가 가장 빠르고 conversion도 가장 높았으며, 또 KOH의 농도는 2mole%일 때 가장 높은 conversion과 점도가 얻어졌다.
50℃에서의 중합은 30℃에서의 중합보다 초기반응속도는 빠르나, 시간이 경과할수록 conversion과 점도가 오히려 낮아지는 경향이 관찰되었다.
최소자승법으로 중합속도를 구하였다.

• 형태사항: 1책(면수복잡) : 삽화 ; 26 cm
• 언어: 한국어
• 일반주기: 저자명의 영문표기 : Jung-Hag Park ; 지도교수의 한글표기 : 최삼권 ; 지도교수의 영문표기 : Sam-Kwon Choi
• 학위논문: 학위논문(석사) - 한국과학기술원 : 화학과,
• 서지주기: 참고문헌 : p. 42-43
• 주제: Telomerization. ; Block copolymers. ; Catalysis. ; 음이온 중합. --과학기술용어시소러스 ; 피롤리돈. --과학기술용어시소러스 ; 촉매. --과학기술용어시소러스 ; 블록 공중합체. --과학기술용어시소러스 ; Addition polymerization.