An investigation has been performed on the effect of high temperature thermomechnical treatment (HTMT) on the mechanical properties, especially strength and toughness of vanadium modified AISI 4330 Steel.
The experimental results showed that HTMT increased the strength and toughness of steel compared to conventional heat treatment. The optimum condition of HTMT was HTMT 54%, in case of which ductile-brittle transition temperature decreased from 2 ℃ of HTMT 0% to - 50 ℃ of HTMT 54%, yield strength was 128 kg/㎟, resulting in the increase of 10% and the fracture mode was ductile fracture mode.
The improvement of mechanical properties by HTMT is due to the distribution of fine carbide precipitates within the martensite lath and the refinement of martensite structure.
본 연구에서는 Vanadium modified AISI 4330 강을 사용하여 고온 가공열처리가 기계적성질, 특히 인성과 강도에 미치는 영향을 조사하였다.
본 연구결과에 의하면 고온가공열처리는 종래의 열처리에 비해 강도와 인성을 증가시키고 있다. 특히 54% 고온가공 열처리한 경우는 고온가공열처리 하지 않은 경우에 비해 취성천이온도는 -50 ℃를 나타내어 52 ℃가 감소하였고 항복강도는 128 kg/㎟를 나타내어 약 10 %가 증가하였으며, fracture mode 는 ductile fracture mode 이었다.
이러한 기계적 성질의 향상은 고온가공열처리가 주로 미세한 석출탄화물을 martensite lath 내에 분포시켰으며, 동시에 martensite조직을 미세화 시켰기 때문이라고 생각된다.