The synthesis of pyrrolidone-N-sulfonyl chloride has been carried out by the reaction of pyrrolidone with sulfuryl chloride in benzene. It was attempted to study the catalytic effect of pyrrolidone-N-sulfonyl chloride as an initiator on anionic polymerization of pyrrolidone. It was found that as a concentration of initiator decreased, inherent viscosity of the resulting polymer increased up to 1.8 dl/g.
The highest rate of polymerization and equilibrium conversion were observed when mole ratio of PNSC to KOH was 0.25. In general, the observed value of rate of polymerization and equilibrium conversion in circumstances using PNSC/KOH catalysis system were higher than using $CO_2$/KOH catalysis system.
Pyrrolidone 음이온 중합의 새로운 개시제로 pyrrolidone-N-sulfonyl chloride를 합성하고 그 개시제로서의 효과를 조사하여 그 결과를 $CO_2/KOH$ catalysis 및 N-acyl type의 initiator와 비교하였다.
중합수율은 60 ∼ 75% 이었고, inherent viscosity는 1∼ 1.8dl/g 이었다.
PNSC/KOH mole ratio가 0.25 부근일때 중합속도가 가장 빠르고 conversion도 가장 높았으며, PNSC의 농도를 적게 가할수록 inherent viscosity가 증가하는 경향을 보였다.
Pyrrolidone-N-sulfonyl chloride의 개시제로서의 효과는 중합속도 및 conversion에 있어서 $CO_2/KOH$ catalysis system 보다 좋은 경향을 보였고, 분자량도 N-acyl type의 initiator 보다 좋은 결과를 관찰할 수 있었다.