A series of crosslinked 2-hydroxyethyl methacrylate (HEMA)-2,3-dihydroxypropyl methacrylate (DMPMA) copolymer membranes for transport experiments has been prepared. The cross-linker used was tetraethyleneglycol dimethacrylate(TEGDMA). Membranes were prepared by polymerizing the monomers as a thin homogeneous film. Using these membranes, relative permeabilities ($U_{re}$) and distribution coefficients ($K_D$) for low aliphatic alcohols and urea were measured. Also diffusion coefficients ($D_m$) and overall fractional coefficients (f) were calculated. In addition, equilibrium water content was measured.
On the basis of hydrophilic interaction, the structural factors of solutes and above experimental data, the transport phenomena of the solutes through the copolymer hydrogel membranes were discussed. The results showed that urea has good permselectivity over the other solutes at the two compositions of 4(DHPMA):6(HEMA) and 2(DHPMA):8(HEMA). And it was revealed that the effect of hydrogen-bonding on diffusion gets more important with decreasing equilibrium water content in polymer matrix.
수송실험을 하기위해 2-히드록시에릴 메타크릴테이트(HEMA)와 2,3-디히드록 시프로필 메타크릴테이트(DHPMA )를 가교 시킨 일련의 공중합체 반투막을 만들었다. 가교제로는 메트라에틸렌글리콥 디메타크릴테이트(TEGDMA )를 사용했다. 반투막은 단량체를 얇은 균일막이 되도록 중합시켜 합성했다.
이 반투막을 이용하여 저급 지방 알콜과 요소에 대한 상대투과율과 분배계수를 측정 했다. 또한 확산계수와 마찰계수도 계산했다. 부가적으로 평형 물 함량을 측정했다.
친수성작용, 용질의 구조적인자, 그리고 위 실험자료를 근거로 하여 용질의 수송현상을 설명했다. 결과에 따르면 조성이 4(DHPMA ): 6(HEMA )와 2(DHPMA ): 8(HEMA )에서 요소가 좋은 투과 선택성을 보여주었다. 또한 확산에 대한 수소결합의 영향은 수화겔 내의 평형 물함량이 감소할수록 그 영향이 점점 커진다는것도 아울러 밝혀졌다.