A laboratory extraction process was studied to obtain a high purity $Al_2O_3$ from low grade Korean Alunite.
Alunite ore was treated by 15% $NH_4OH$ solution, followed by 10% $H_2SO_4$ leaching and metallic impurities such as Fe and Ti in sulfate solution were removed by solvent extraction.
Alumina obtained by the extraction process was more than 99% in purity.
To obtain fine alumina powder from $NH_4Al(SO_4)_2$ extracted from Alunite and chemical reagent $Al_2(SO_4)_3$ $17H_2O$, Hot Petroleum Drying (H.P.D.) Method was employed.
The sinterbility of alumina powder prepared by H.P.D. method compared with one treated by other methods was shown to be improved, but dry compaction was difficult due to the aggloromeration of powder.
Hot Petroleum Drying method is considered to be a practical method for laboratory scale to make a chemically homogeneous and fine powder.
저품위의 국산 명반석으로부터 고순도의 $Al_2O_3$ 를 얻기 위한 실험실적 추출방법을 연구하였으며, 또한 이 방법으로 얻은 $Al_2O_3$에 대한 소결성을 조사하였다.
명반석을 15% $NH_4OH$ 용액으로 침출한 후 다시 10% $H_2SO_4$로 침출하였으며, Fe 나 Ti 같은 불순물은 Solvent extraction 방법으로 제거하였다.
추출하여 얻은 $Al_2O_3$의 순도는 99% 이상이었다.
명반석에서 추출한 $NH_4Al(SO_4)_2$와 시약급의 $Al_2(SO_4)_3\cdot 17H_2O$로 부터 석유증발법을 사용하여 미세한 분말을 제조하였고, 이렇게 만든 $Al_2O_3$ 분말의 소결성은 다른 방법으로 제조된 분말에 비해 더 좋았으나 미세한 분말의 응집상태 때문에 건조성형이 용이하지 않았다.
석유증발법은 화학적으로 균일하며 입자가 미세한 분말을 제조하는 실험실적인 방법으로서 실용적인 것으로 믿어진다.