The catalytic reduction of nitric oxide by ammonia was studied over Cu(II)-ion exchanged Y, X, A type Zeolites and Mordenite.
The order of activity was found to be $CuX ＞ CuY ≫$ Cu-mordenite$\approx$CuA, and in each case the catalytic activity showed reversible bell shaped temperature dependence with maximum between the temperature of 100˚- 140℃.
Temperature programmed desorption and E.P.R measurement indicated that in the case of CuX and CuY Cu(II)-tetraammine complex was formed which acted as an active center, but not in the case of CuA and Cu-mordenite.
It was also found that in the case of CuX and CuY, ammonia coordinated with Cu(II) was partially desorbed at about 120℃ where the reaction rate began to decrease.
Therefore, it may be thought that decrease in the activity at high temperature is duc to the destruction of active center at elevated temperature, and difference in the activity among various types of zeolites is due to the difference in the extent of Cu(II)-tetraammine complex formation and its stability.
Cu(II)로 이온교환한 Y-형, X-형, A형 Zeolite 와 mordenite 촉매상에서 암모니아에 의한 일산화질소의 환원반응에 관하여 고찰 하였다. 촉매의 활성은 $Cu-X ＞ Cu-Y ≫ Cu-$ mordenite $\approx$ Cu A 의 순이었고 이들모두는 100 ˚ ~ 140 ℃ 에서 최대활성을 나타내다가 그이상의 온도에서는 점차 활성이 떨어지는 가역적이고 종모양의 온도의존성을 나타냈다. T.p.D 와 E.p.R 측정의 결과를 보고 반응조건에서 활성이 좋은 Cu- X, Cu- Y 의 경우는 이반응에서 실제적인 활성점으로 작용하는 Cu(II) - tetra ammine Complex 가 잘 형성되나 Cu - A, Cu - mordenite 의 경우에는 그렇지 못했다.
그리고 Cu X, Cu Y의 경우를 보면 반응속도가 감소하기 시작하는 온도인 120 ℃ 근처에서 Cu(II)에 배위된 암모니아의 부분적 탈착이 일어남을 볼 수 있었다.
그러므로 높은온도에서의 활성감소는 온도가 높아지면 활성점이 파괴되기 때문이라고 볼수 있으며 담체의 종류에 따른 활성변화는 담체에 따라 Cu(II) - tetraammine Complex 가 형성되는 정도나 그 안정도가 달라지기 때문이라고 생각할수 있다.