ZnO single crystals are grown by vapor phase reaction with pure Zn metal as Zn-vapor source. Crystals obtained are mainly needles 20mm in length, platelets 8㎟ in area, or pyramids 2mm in height.
Patterns suggesting their growth mechanism are observed in their microphotographs. The present experiments show that in the needle-like growth, the complete $\{10\bar{1}0\}$ surfaces develop from the root to the tip and from the edges toward the center.
In the plate-like growth $〈2\bar{11}0〉$ main arm is elongated, and 〈0001〉 whiskers are grown on the main arm. Then the platelet is completed. At the same time, $(000\bar{1})$ plane is thickened by layers. The layers nucleate at the edges of $(000\bar{1})$ plane to proceed towards the center. Before the initially generated layers reach the centeral part, the new layers are generated on those layers. As the layers proceed towards the centeral, part, the curvelinear growth front develops from the linear growth front, which forms the terraced $(000\bar{1})$ surface.
아연증기원으로 순수한 아연 금속을 사용하여 산소와 반응시키는 기상반응법을 이용하여 산화아연 단 결정을 키웠다. 얻어진 단 결정은 주로 길이 20 mm 정도인 needle, 면적 $8 mm^2$ 정도인 platelet,높이 2 mm 정도인 pyramid이다.
단 결정의 성장기구를 추정하기 위하여 성장 양상을 현미경으로 관찰하였다. 본 실험에서 확인한 바로는, 침상결정성장에 있어서 $\{10\bar{1}0\}$ 면은 밑 부분에서 끝 부분으로, 모서리에서 안쪽으로 갈수록 완전한 flat-habit가 나타난다.
또 판상결정성장에 있어서는 먼저 $〈2\bar{1}\bar{1}0〉$ main arm이 자라난 다음, 〈0001〉 whisker 가 그 main arm 위에 자라나서 platelet를 형성하게 된다. 이와 동시에 $(000\bar{1})$ 면은 $(000\bar{1})$ 면에 나란한 layer에 의하여 두꺼워 지는데, 이들 layer는 $(000\bar{1})$ 면의 모서리에서 생겨나서 $(000\bar{1})$ 면의 안쪽으로 진행한다. 먼저 생겨난 layer가 중앙부위에 이르기 전에 새로운 layer가 먼저 생겨난 layer위에 계속하여 생겨난다. 이들 layer는 중앙부위로 진행해 감에 따라 layer 의 linear growth front 는 curvelinear growth front 로 되어, 중앙에 구릉을 남기는 terraced$(000\bar{1})$ surface를 형성하게 된다.