The object of this study is to improve the durable antistatic property of the synthetic fibers, especially, nylon-6 fiber of which electrical conductivity is very low.
In general, since the poor electrical conductance of nylon6 fiber is due to its hydrophobicity, we can reduce the build-up of static change on the fiber surface and increase the electrical conductivity of fiber yarn by applying the hygroscopic material, such as poly (ethylene oxide), on nylon-t fiber.
Then, the antistatic property of nylon-t fiber, of which the electrical conductance is increased by the above method, decreases gradually during washing or dry cleaning.
Therefore, the following method was used to increase the durability of the antistatic property in this study.
At first, the end group of poly (ethylene oxide), hydroxyl group, is replaced by the carboxyl group.
Then, it reacts with the amine end group of polycaprolactam.
The poly (ethylene oxide), applied to polycaprolactam by the chemical bonding like this, is not easily extracted by water during washing.
Therefore, the nylon-6 fiber can obtain the durable antistatic property.
합성섬유, 특히 전기 전도성이 좋지 않은 nylon-6 fiber 의 전기적 성질을 개선하고자 하는 것이 본 연구의 목적이다.
우선 hygroscopic material 인 poly (ethylene oxide) 를 nylon fiber 에 도입함으로써 fiber surface 의 static charge 의 발생을 줄이고, 또한 fiber yarn 의 전기 저항을 줄일 수 있다.
그런데 이렇게 해서 일단 전기 전도성이 향성된 nylon fiber 의 antitatic property 는 실제로 사용함에 따라 점점 감소하게 된다. 그래서 보다 오랫동안 antistatic property 를 지닐 수 있도록 하기 위하여 본 실험에서는 다음과 같은 방법을 이용하였다.
즉, poly (ethylene oxide) 의 end group 인 hydroxyl group 을 carboxyl group 으로 바꾸어서 polycaprolactam 의 amine group 과 결합시키는 방법이다.
이와 같은 화학 결합을 통하여 polycaprolactam 에 도입된 poly (ethylene oxide) 는 물에 의해서 쉽게 추출되지 않는다. 그러므로 nylon-6 fiber 의 antistatic property 는 상당히 오랫동안 유지될 수 있는 것이다.