The epoxy cure was observed by ultrasonic longitudinal velocity measurements at 19, 40, and 110℃ of curing temperatures. Three types of phase transition behavior of epoxy resin were due to the elastic modulus change during the cure of epoxy resin.
Photoacoustic(PA) and thermoacoustic measurements were used to observe the curing of epoxy resin at 40℃ of ambient temperature. Five stages in PA and thermoacoustic signals showed the usual transition of liquid → rubber → glass state due to gelation and following vitrification. The variation of thermal diffusivity obtained by the phase-lag method also showed the five stage transitions reflecting the change of thermal properties.
에폭시 큐어링 과정을 주위온도 40℃에서 초음파 속도 및 광음향과 thermoacoustic측정으로 관찰하였다. 세가지 측정결과 epoxy resin의 큐어링 동안에 gelation과 vitrification에 의하여 elatsic modulus와 thermal diffusivity가 변화하여 Liquid → rubber → glass state transition 의 5stage를 볼 수 있었다. 여러가지 주위온도에서 에폭시 큐어링동안에 세가지 형태의 transition을 초음파속도로 측정하였다. glass transition 이상의 높은 주위온도에서 Liquid → rubber transition 이 일어났고, 낮은 온도에서 Liquid → glass transition 이 일어나고 있음을 Liquid → rubber → glass transition 동안의 초음파속도 측정결과와의 비교로 알 수 있었다.