Poly(2-cyano-5-methoxy-1, 4-phenylenevinylene), PCMPV, and a series of PPV copolymers containing 2-cyano-5-methoxy-1, 4-phenylenevimylene (CMPV) units were prepared via the water-soluble precursor method. They were obtained in film form and were doped with $FeCl_3$. Doping of undrawn and drawn film of PCMPV homopolymer with $FeCl_3$ led to conductivity of $9.1\times10^{-5}-7.2\times10^{-4}$ S/cm. Conductivity of $FeCl_3$ doped copolymer films ranged from $3.0\times10^{-4}$ - 4.1 S/cm depending on composition. The copolymer containing very low level (~ 5 mole %) of CMPV unit revealed the highest conductivity among the copolymer compositions. On the other hand precursor polymer films of PCMPV and 35PCMPV were cast from water solution onto tin-oxide coated glass, the nonlinear optical chromophores in the polymer films were aligned by corona discharge poling, and nonlinear optical properties were investigated. The resulting electro-optic coefficients of PCMPV and 35PCMPV were $3.5\times10^{-8}$ e.s.u. (1.16 pm/V) and $3.0\times10^{-8}$ e.s.u.(1.06 pm/V), respectively.
폴리 (2-시아노-5-메록시-1,4-페닐렌비닐렌) (PCMPV) 및 PCMPV와 PPV의 공중합체를 수용성 선중합체를 거처 필름 형태로 합성하였다. 원소분석을 통하여 공중합체의 조성을 결정하였으며 UV-VIS, IR, DSC, TGA를 이용하여 필름의 구조 및 특성을 분석하였다.
최종 중합체를 상온에서 $FeCl_3$로 도핑한 결과 PCMPV는 연신시킨 것과 연신시키지 않은 것이 각각 $7.2\times10^{-4}$ S/cm와 $9\times10^{-5}$ S/cm의 전기 전도도를 나타냈으며 공중합체는 조성에 따라 $3.0\times10^{-4}$ - 4.1 S/cm의 전기 전도 범위를 보였다. 5배 연신시킨 필름은 연신시키지 않은 것에 비해 약 10배 정도의 전도도를 보였으며 5몰 퍼센트의 PCMPV 함량을 가진 공중합체 필름이 최대의 전기 전도도를 나타내었다. PCMPV와 35PCMPV(35몰 퍼센트의 PCMPV 조성)의 선중합체를 틴-옥사이드가 입혀진 유리위에 캐스팅한 다음 코로나 폴링시켜 비선형 광학 특성을 조사하였다 PCMPV와 35PCMPV의 선중합체 필름으로부터 얻어진 전기-광학 계수는 각각 1.16 pm/V와 1.06 pm/V였다.