We demonstrated that the photoluminescence (PL) from the europium (Eu) organometallic complex can be enhanced by the plasmonic effect in the conventional organic light emitting diode (OLED) structure from an anode to an emissive layer with solution processing. The existence of the aggregated gold nanoparti-cles (A-Au NPs) can modify the PL property of the Eu organometallic complex and increased the PL intensity around main emission peak at 614 nm as 31% according to the increase of the A-Au NP concentration from 0 mM to 1.86 mM. Because the aggregation of the gold nanoparticles (Au NPs) creates a new plasmonic band in the range of the red wavelength in comparison to the Au NPs, the deep spectral overlap between extinction of the A-Au NPs and emission band of the Eu organometallic complex makes resonant coupling stimulate the spontaneous emission rate of an emitting center. The enhancement factor elucidating the effect of A-Au NPs was calculated, which is obtained values by dividing the integrated PL intensity of the samples incorporated A-Au NPs by that of a reference sample without A-Au NPs. The enhancement factor consistently increased as the concentration of A-Au NPs increases, saturated over more than 1.24 mM of A-Au NPs. In addition to the change of the emission intensity on the addition of metallic nanoparticles, we observed the variation of the asymmetric ratio (AS) value with the concentration of the A-Au NPs, defined as the integrated emission intensity ratio electric dipole transition (5D0
기존의 용액 공정 가능한 organic light emitting diodes (OLEDs)의 양극부터 발광층까지의 구조에서 유로피엄 유기 복합물의 photoluminescence (PL)가 plasmonic effect에 의해 향상될 수 있음을 증명하였다. 뭉친 금 나노 입자는 유로피엄 유기 복합물의 PL특성을 변화시킬 수 있었고, 뭉친 금 나노 입자의 농도가 0 mM에서 1.86 mM까지 증가함에 따라 주요 발광 부분인 614 nm에서의 발광 세기가 31% 증가하였다. 금 나노 입자의 뭉침 현상은 뭉치지 않은 금 나노 입자에 비해 red wavelength영역에서 plasmonic band를 형성하기 때문에, 뭉친 금 나노 입자의 extinction과 유로피엄 유기 복합물의 발광 밴드간의 겹침 현상은 resonant coupling을 통해 발광 물질의 자발광률을 향상시킨다. 뭉친 금 나노 입자로 인한 효과를 설명하기 위해, 뭉친 금 나노 입자가 삽입된 샘플의 적분된 PL세기를 뭉친 금 나노 입자가 삽입되지 않은 샘플의 적분된 PL세기 값으로 나눠준 enhancement factor를 계산하였다. Enhancement factor값은 뭉친 금 나노 입자의 농도가 증가함에 따라 계속하여 증가하였으며 1.24 mM을 지남에 따라 포화되는 경향을 나타내었다. 이처럼 금속 나노 입자의 첨가에 따른 발광 세기의 변화 이외에도, 우리는 electric dipole transition (5D0