High temperature solid oxide fuel cell (SOFC) has prospect and potential to generate electricity from fossil fuels with high efficiency and very low greenhouse gas emissions as compared to traditional thermal power plants. In the last 10 years, there has been significant progress in the materials development and stack technologies in SOFC. The objective of this dissertation is to characterize the redox properties of anode-supported tubular SOFC.
In chapter III, redox behavior of a Ni??Y2O3-stabilized ZrO2 (YSZ) composite anode support and the performance degradation of an anode-supported tubular solid oxide fuel cell (SOFC) were studied under complete oxidation and reduction conditions (degrees of oxidation and reduction = 100%). Materials characterization studies showed that the exposure time in oxidizing and reducingatmospheres played a critical role in the degradation of the porous structures and the physical properties of the anode support. In particular, the redox cycling with an 8 h exposure time resulted in the cracking of YSZ network, leading to significant decay of the mechanical strength. The polarization experiments on the redox-cycled anode-supported tubular cell showed serious performance
High temperature solid oxide fuel cell (SOFC) has prospect and potential to generate electricity from fossil fuels with high efficiency and very low greenhouse gas emissions as compared to traditional thermal power plants. In the last 10 years, there has been significant progress in the materials development and stack technologies in SOFC. The objective of this dissertation is to characterize the redox properties of anode-supported tubular SOFC.
In chapter III, redox behavior of a Ni??Y2O3-stabilized ZrO2 (YSZ) composite anode support and the performance degradation of an anode-supported tubular solid oxide fuel cell (SOFC) were studied under complete oxidation and reduction conditions (degrees of oxidation and reduction = 100%). Materials characterization studies showed that the exposure time in oxidizing and reducingatmospheres played a critical role in the degradation of the porous structures and the physical properties of the anode support. In particular, the redox cycling with an 8 h exposure time resulted in the cracking of YSZ network, leading to significant decay of the mechanical strength. The polarization experiments on the redox-cycled anode-supported tubular cell showed serious performance