In this paper, arc characteristics of narrow groove joints using pulsed GMA welding were found out. The bevel angles of 22.5˚ and 30.0˚ were considered and with those angles two kinds of weld configurations, all two sides were 22.5˚ or 30.0˚. Typically, the narrow groove needs less deposited metal so it has less heat input than normal wider groove. In this reason, narrow groove has some advantages of less welding distortion and less thermal effects. In the experiment, workpiece made by one groove angle rather than by two ones was used and the welding current and voltage were measured to investigate arc characteristics. As a result, welding current was changed abnormally around groove edge. Namely, as the arc moved close to groove face, welding current was increased rapidly because arc was affected by inclined face. Based on understanding those phenomena, more reliable applications to seam tracking will be possible.
이 논문에서는 pulsed GMA용접에서의 narrow groove joint의 아크특성에 관하여 연구하였다. Pulsed GMAW는 입열량이 작고, 높은 용접품질을 얻을수 있으며 적은 스패터의 장점을 가진다. Narrow groove는 기존의 groove와 비교하여 상대적으로 열입력이 적어 열에 의한 변형이 작다는 장점이 있다. 각 연구는 bevel angle이 22.5˚, 30˚에서의 아크특성과 groove angle이 45˚, 60˚의 아크특성에 관하여 연구하였다. 용접신호를 측정하여 아크특성에 관하여 연구하였다. 아크는 groove edge이전에 groove face로 이동되는 특이한 현상을 보인다. 이러한 현상은 용접전류의 급격한 감소를 가져온다. 이동된 아크는 groove face를 따라 이동되면서 용접전류는 선형적인 증가를 보인다. groove angle이 45˚, 60˚ 실험에서 root gap의 크기에 따라 아크는 molten pool의 영향을 받는다. Groove angle이 45˚인 경우 아크의 이동이 심하여 molten pool의 영향을 상대적으로 덜 받는다. Narrow groove일수록 아크의 이동이 뚜렷한 경향을 보인다. 이러한 현상을 고려하면 보다 정확한 용접선 추적이 가능할 것이다.