액상이 게재된 $BaTiO_3$ 의 분위기에 따른 입자성장 양상 = Grain growth behavior of $BaTiO_3$ in $SiO_2$ -rich liquid matrix
서명 / 저자 액상이 게재된 $BaTiO_3$ 의 분위기에 따른 입자성장 양상 = Grain growth behavior of $BaTiO_3$ in $SiO_2$ -rich liquid matrix / 장재명.
저자명 장재명 ; Chang, Jae-Myung
발행사항 [대전 : 한국과학기술원, 2005].
Online Access 원문보기 원문인쇄

소장정보

등록번호

8016130

소장위치/청구기호

학술문화관(문화관) 보존서고

MAME 05027

SMS전송

도서상태

이용가능

대출가능

반납예정일

초록정보

The present investigation studies the solid/liquid interface structure between $BaTiO_3$ and a $SiO_2$ -rich liquid with atmosphere and its effect on the microstructure. A (100) $BaTiO_3$ single crystal was embedded in a $5mole%-SiO_2-excess$ $BaTiO_3$ powder compact and sintered at 1280 ℃ under various oxygen partial pressures $(0.2 atm ~ 10^{-24} atm)$. During sintering, the single crystal grew into the fine matrix and trapped isolated liquid. The shape of the entrapped negative crystal was rounded i.e. interfacial step free energy decreased as the oxygen partial pressure decreased. The microstructural evolution of $10 mole%-SiO_2-excess BaTiO_3$ at 1280 ℃ was also observed under various oxygen partial pressures by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope(TEM). The grain growth mode changed dramatically with the interface structure from stagnant, abnormal, to normal. In the case of stagnant grain growth, apparent growth exponent was about 110 in contrast to 3 for normal grain growth in a reducing atmosphere. An intergranular liquid film was observed between the fine matrix grains. Abnormal grain growth was observed in a specimen sintered under an intermediate atmosphere $(P_{O2}~10^{-20} atm)$ as at an increased temperature of 1300 ℃. The observed grain growth behavior was explained in terms of the step free energy of the interface and the driving force for grain growth. Stagnant grain growth is believed to occur when the step free energy is very large so that the critical driving force is larger than the driving force for the growth of the lager grain. On the other hand, stagnant and abnormal grain growth can occur when the driving force is comparable to the critical driving force. Normal grain growth occurs when the driving force for grain growth is larger than the critical driving force.

$SiO_2$ 액상이 게재된 $BaTiO_3$ 의 분위기에따른 고/액 꼐면의 모양변화와 그에 따른 입성장 양상을 연구하였다. (100) $BaTiO_3$ 단결정을 이용하여 액상이 포획된 음결정의 분위기에 따른 모양변화를 관찰한 결과, 환원 분위기로 진행됨에 따라 고/액 계면이 둥글어 짐을 확인할 수 있었고, 이로 분위기에 따른 step free energy의 변화를 유추해 볼 수 있었다. 입성장 양상은 분위기에 따라 매우 독특하게 변화하였는데 공기 중에서 소결한 시편에서는 입성장이 거의 발생하지 않았고, 환원 분위기에서는 정상입성장이 발생하였으며, 그 중간 분위기에서는 비정상 입자 성장이 일어났다. 이는 이차핵생성/성장의 임계자유에너지가 분위기에 따라 감소함에 따른 변화라 생각된다.

서지기타정보

서지기타정보
청구기호 {MAME 05027
형태사항 [ii], 69 p. : 삽도 ; 26 cm
언어 한국어
일반주기 저자명의 영문표기 : Jae-Myung Chang
지도교수의 한글표기 : 강석중
지도교수의 영문표기 : Suk-Joong L. Kang
학위논문 학위논문(석사) - 한국과학기술원 : 신소재공학과,
서지주기 참고문헌 : p. 65-69
주제 입성장
step 자유에너지
바륨타이타네이트 지향적 의미구조
아이디어 전개 지원도구
Grain growth
Step free energy
$BaTiO_3$
surface-functionalizationriented sementic association model
idea development tool