The materials containing selenium have recently been attracting much attention in light emitting diode(LED) and field effect transistor (FET).We have synthesized a new soluble conjugated copolymer (F8Se2) derived from 9,9-dioctylfluorene and 2,2-biselenophene by the palladium-catalyzed Suzuki coupling reaction. The synthesized polymer was characterized by $^1H$ NMR, UV-vis spectroscopy, PL, TGA and GPC. Also, we confirmed that F8Se2 is thermotropic liquid crystalline polymer with aligned structure from DSC, PLM and XRD analysis. EL device constructed with configuration of ITO/PEDOT:PSS/polymer/Ca/Al exhibited high brightness (1200 cd/㎡) at 10.5 V and low turn-on voltage (3.5 V). The significant red shift of the emission of Se-containing copolymer in comparison with its sulfur analogue, poly-9,9-dioctylfluorene-alt-bithiophene (F8T2), is attributed to the electron-donating property of selenium and strong interaction between biselenophene moiety in neighboring copolymer chains. Also, solution-processed FET of F8Se2 polymer was successfully fabricated using bottom-contact geometry and showed the typical p-channel field effect transistor characteristics. The measured field effect mobility of the transistor was $0.5×10^{-2}㎠/Vs$ and the on/off ratio was $1 ×10^4$.
스쯔끼 중합을 통하여 C-9위치에 옥틸기를 갖는 플루오렌기와 셀로노펜기를 갖는 새로운 공중합체 F8Se2를 성공적으로 합성하였다. 합성된 고분자의 수 평균 분자량은 76,000이고, $^1H$ NMR 과 $^{13}C$ NMR 과 원소분석으로 구조를 확인할 수 있었으며, 420℃ 까지 안정된 열 안정성을 보였다. 또한 F8Se2 고분자는 DSC, PLM, XRD분석를 통해서 액정상에서 자발적인 분자 배열을 갖는 열방성 액정 고분자임을 확인하였다.
ITO/PEDOT/F8Se2/Ca/Al의 적층 구조로 이루어진 소자에서는 최대 밝기가 1200cd/㎡인 (0.54, 0.46) 색 좌표의 오렌지색 광을 얻었다. 이러한 스펙트럼의 결과는 셀레노펜을 싸이오펜으로 대치한 고분자의 경우보다 장파장 쪽으로 이동한 것으로, 싸이오펜보다 크기가 큰 셀레노펜이 고분자 사슬간에 더 강한 상호 반응을 하는 것을 알 수 있다. 이러한 특성을 살려서 F8Se고분자를 유기 전계 효과 트랜지스터에 적용하였고, $0.5×10^{-2}㎠/Vㆍs$ 의 이동도를 나타내었다.