A series of derivatives of 4-(Dicyanomethylene)-2-methyl-6-[p-(dimethylamino) styryl]-4H-pyran (DCM) have been synthesized by Knoevenagel condensation and they have been characterized with NMR, UV-visible and photoluminescence study. The electrolumnescent devices have been fabricated as typical single-layer devices consisting of ITO/polymer film/Al. The polymer films consist of a host polymer, poly(N-vinylcarbazole) which transport holes, a electron transporting material, 2-(4-biphenylyl)-5-(4-tert-butylphenyl) 1,3,4- oxadiazole (PBD), and the dopants, DCM derivatives. The device in which the concentration of dopant, (2,6-Bis{2-[4-(dibutylamino)phenyl]vinyl}-4H-pyran-4-ylidene)methane-1,1-dicarbonitrile (DCM2NBu), is 5 wt%, shows the pure red emission with the CIE coordinate, (0.66, 0.33), and the maximum emissive wavelength, 643 nm. The turn-on voltage of the device is $1.4×10^{8} V/m$.
Knoevenagal 축합 반응에 의해 여러가지 4-(Dicyanomethylene)-2-methyl-6-[p-(dimethylamino)styryl]-4H-pyran (DCM) 유도체를 합성하였다. 긴 알킬사슬을 가진 유도체들은 $CHCI_3$, THF, 톨루엔, 사이클로헥산온 등 일반적인 유기용매에 잘 녹았고, 그 중 pyran ring에 한쪽으로 축합된 유도체보다 양쪽으로 축합된 유도체들은 좋은 박막성질을 가지고, 열적으로 훨씬 안정하였다. 양쪽으로 축합된 DCM2NMeOEH, DCM2NBu, DCM2NHex 는 기존의 적색발광물질로 사용된 DCM 보다 20 nm 정도 장파장쪽으로 이동한 620 nm 근처에서 최대발광을 보였다.
폴리비닐카바졸에 전자수송물질인 PBD 와 DCM 유도체들을 도핑한 후, 그것을 ITO 위에 스핀코팅하고 다시, 그 위에 알루미늄전극을 진공증착하여 전기발광소자를 제작하였다. 도핑제의 농도에 따라 최대발광파장이 장파장으로 이동하였으며, DCM2NBu 의 경우 5 wt% 도핑한 소자에서 최대발광파장이 643nm 이고, CIE 좌표로 (0.66, 0.33) 인 순수한 적색을 나타내었다. 밝기는 DCM으로 제작된 소자와 비슷하고, 따라서 기존의 적색발광 물질을 대체할 도핑제로서 양쪽으로 축합된 DCM 유도체를 제안한다.