Poly[2,5-bis(trimethylsilyl)-alt-2-methoxy-5-(2-ethylhexyloxy)- p-phenylenevinylene] (DSi-alt-MEHPPV), Poly[2,5-bis(trimethylsilyl)- alt-2,5-methoxy-p-phenylenevinylene] (DSi-alt-DMOPPV) and poly[dithieno(3,2-b:2',3'-d)thiophene]- p-vinylene-alt-2-methoxy-5-(2-ethylhexyloxy)bezene- p-vinylene] (DTT-MEH) have been synthesized by Wittig condensation polymerization. These polymers were characterized by using $^{1} H$ NMR, FT-IR spectros-copy. These polymers have good solubility in organic solvents. The $π-π^{*}$ transition peaks of DSi- alt-MEHPPV, DSi-alt-DMOPPV and DTT-MEH appeared at 400, 390 and 500 nm, respectively. The EL device was fabricated by typical single-layer device consisting of ITO/polymer/Al. The EL emission peak of DSi-alt-MEHPPV was shown at 537 nm, and that of DSi-alt-DMOPPV was 530 nm. The emission maximum of DTT-MEH appeared at 680 nm indicating red light emission. DSi-alt-MEHPPV, DSi-alt-DMOPPV and DTT-MEH have turn-on voltages for current at 15, 17 and 5 V, resectively.
Wittig 축합 중합을 통하여 DSi-alt-MEHPPV, DSi-alt-DMOPPV, DTT-MEH의 세가지 고분자를 합성하였다. 이들의 고분자는 FT-IR, UV-visible, TGA 열분석 등으로 특성을 조사하였다. 고분자의 분자량은 각각 $M_n = 4,400$, $M_w = 5,000$ (DSi-alt-MEHPPV), $M_n = 5700$, $M_w = 7400$ (DSi-alt-DMOPPV), $M_n = 4,900$, $M_w = 6,200$(DTT-MEH) 였다. 이들 고분자는 용매에 잘 녹았다. 고분자들의 $π-π^{*}$ 흡수 피크는 400, 390, 500 nm였다. EL 장치는 일반적인 방법으로 고분자 필름은 스핀 코팅에 의해서 만들고, 알루미늄을 음극으로 사용하였다. 고분자들의 EL 성질은 EL 스펙트럼, 전류-전압-빛의 세기 성질을 조사하였다. 최대 발광 파장은 DSi-alt-MEHPPV에서는 537 nm, DSi-alt-DMOPPV에서는 530 nm에서 나타났다. DTT-MEH의 경우에는 적색영역인 680 nm에서 나타났다. 그리고 이 것은 DTT 기 때문에 DSi-alt-MEHPPV나 MEH-PPV보다 적색영역에서 발광한다. 각각 고분자의 구동 전압은 15 (DSi-alt-MEHPPV), 17 (DSi-alt-DMOPPV), 6 V(DTT-MEH)에서 나타났다.