A new diamine monomer containing cyano group, 2-cyano-4,4'-diaminophenyl ether, was synthesized and polymerized to polyimides with several aromatic anhydrides via two kinds of imidization methods, namely, thermal or solution imidization methods. By the thermal imidization method, tough, flexible and creasable polyimide films were obtained, except the polyimide from pyromellitic dianhydride. The polyimides had high $T_g$ values and they are stable up to 500℃ in air. The polyimides prepared by solution imidization method are partially soluble in polar aprotic solvent with heating, but the reprecipitated polymer after dissolved in concentrated $H_2SO_4$ were well dissolved in polar aprotic solvents.
Four kinds of core molecules, which have tetra- or octa-hydroxyl functional group, were synthesized from bisphenol A, 4,4'-biphenol and hydroquinone. These cores and neopentyl glycol were used as an initiator for the stannous octoate catalyzed living ring opening polymerization, and linear and star poly(e-caprolactone)s were synthesized. The linear polymer is more viscous than star polymers with similar molecular weights. Melting points of the polymers decreased with the increasing number of arms and decreasing DP. The 10% weight loss temperature is dependent on molecular weight but not on the number of arms.
N,N-Substituted acrylamides including N-acryloylpiperidine (N-AP), N-phenyl acrylamide (PAA), and N-methyl-N-phenyl acrylamide (MPAA) were polymerized in various conditions using trialkylaluminums. N,N-Substituted acrylamide monomers were prepared from acryloyl chloride with piperidine, aniline and N-methylaniline, respectively. Polymerization of N,N-substituted acrylamides is faster at high temperature than at low temperature, except PAA. The molecular weights of the polymers initiated by triethylaluminum are higher than those of the polymers initiated by tyriisobutylaluminum.
시아노기를 포함하는 새로운 다이아민 단량체인 2-시아노-4,4'-다이아미노페닐 에테르를 합성하였고 합성된 단량체는 몇 가지 방향족 테트라카르복시산이무수물과 함께 열 이미드화와 용액 이미드화의 2가지 방법을 사용하여 폴리이미드로 중합하였다. 열 이미드화 방법을 통해서 질기고 유연하며 깨지지않고 접을 수 있는 폴리이미드 필름을 얻었다. 합성된 폴리이미드들은 높은 Tg값을 가지며 공기중에서도 500℃ 이상까지 안정하였다. 용액 이미드화 방법으로 만들어진 폴리이미드는 가열해주면 극성 비양성자성 용매에 부분적으로 용해되지만, 진한 황산에 녹인 후 재 침전된 고분자는 극성 비양성자성 용매에 잘 용해되었다. 비스페놀 A, 바이페놀 그리고 하이드로퀴논으로부터 4개 또는 8개의 하이드록시기를 가지고 있는 4종류의 핵 분자를 합성하였다. 합성된 핵 분자들과 네오펜틸글리콜을 개시제로 사용하고 틴 옥토에이트를 촉매로 하여 e-카프로락톤을 리빙 개환 중합하여 선형과 성형의 폴리(e-카프로락톤)을 합성하였다. 유사한 분자량을 가진 경우 선형 고분자가 성형 고분자보다 점도가 높으며 고분자의 가지수가 늘어날 수록, 그리고 중합도가 감소할수록 녹는 점은 감소하였다. 10% 질량감소온도는 분자량에 따라 증가하지만 고분자의 가지수에는 무관하였다. 트리알킬알루미늄을 사용하여 N-아크릴로일피페리딘 (N-AP), N-페닐 아크릴아마이드 (PAA) 그리고N-메틸-N-페닐 아크릴아마이드 (MPAA)의 3가지 N,N-치환된 아크릴아마이드를 다양한 조건에서 중합하였다. 아크릴아마이드의 중합은 PAA를 제외하고 저온에서보다 고온에서 더 빠르게 진행되었다. 트리에틸알루미늄에 의해 개시된 폴리머가 트리리소부틸알루미늄에 의해 개시된 폴리머보다 높은 분자량을 가졌다.