Alkylstyryl carbazole group contained poly(methacrylate) (Cz-PMA) was synthesized through radical polymerization route under nitrogen atmosphere. This polymer was characterized with UV-visible, photoluminescence, and electroluminescence study. The EL device was typical three-layer device consisting of ITO / polymer film / Al. The absorption maximum and edge of alkylstyryl carbazole lumophore exhibited at 340 and 400nm, respectively. And Cz-PMA was blended with poly[2-methoxy-5-(2-ethylhexyloxy)-1,4-phenylenevinylene] (MEH-PPV) ; blend ratio was 1/1 and 1/10 (MEH-PPV/Cz-PMA). Absorption peaks of the polymer blends appeared at 340 and 500 nm corresponding to their component polymers. Photoluminescence maximum peak of Cz-PMA appeared at around 440 nm. The polymer blends showed two isolated emission peaks at 440 and 560 nm corresponding to their component polymers. Electroluminescence maximum peaks of 1/1 and 1/10 exhibited at 600 and 580nm.
알킬스티릴 카바졸기를 포함한 폴리메타아크릴레이트(Cz-PMA)를 라디칼 중합을 통해 합성하였다. 이 고분자는 UV-visible, 광발광, 전기 발광 현상 등을 이용하여 그 특성을 조사하였다. 고분자의 수평균 분자량이 14,000 이고 무게평균 분자량은 180,000 정도로 큰 편이고 사이클로헥사논에 쉽게 녹았다. EL 장치는 양극으로 ITO를 사용하였고 음극으로는 알루미늄을 사용하였다. 또 주사슬이 다공액화 되어진 고분자 폴리[2-메톡시-5-(2-에틸헥실옥시-1,4-페닐렌비닐렌] (MEH-PPV)와 블랜드하였다. 고분사 필름은 용액으로부터 spin casting에 의해 만들었다. Cz-PMA의 최대 흡수는 340 nm, 블랜드된 고분자의 경우는 각각의 고분자의 최대흡수에 해당하는 영역에서 두종의 흡수봉우리를 나타내었다. 블랜드된 고분자의 전기발광 스펙트럼은 580-600nm 에서 나타났고 이것은 MEH-PPV에 해당하는 빛으로 Cz-PMA의 색은 나타나지 않았다. 이로부터 여기된 Cz-PMA로에서 MEH-PPV로 에너지 전이가 일어남을 알 수 있다.