Soybean oil-based material is presently attracting interest as a sustainable alternative to crude oil-based materials. However, soybean oil-based non-isocyanate polyurethane (NIPU) commonly encounter challenges in attaining high stiffness as because of large molecule size and irregular structure of CSBO molecule. In order to create a stiff property by forming intersegmental order, poly(2-aminoethylmethacrylate-ran-ethylmethacrylate) (poly(AEMA-ran-EMA)) was used as amine terminated reactant. By analyzing the glass transition temperature in differential scanning calorimetry (DSC) and the position of the halo peak in X-ray diffraction (XRD), it was verified that NIPU, which was derived from a copolymer with a low$_{FAEMA}$ value, has a comparable intersegmental structure to poly(ethyl methacrylate). The synthesized NIPU sample exhibited a Young's modulus that was four-fold more and a tensile stress that was two-fold greater compared to the previous soybean oil-based NIPU. The composition ratio of copolymer can be adjusted extensively and continuously, resulting in a wide variety of Young's modulus and tensile stress values that differ by more than 10 times.
콩기름 기반 재료물질은 현재 원유 기반 재료물질에 대한 지속 가능한 대안으로서 높은 관심을 끌고 있다. 그러나, 대부분의 콩기름 오일 기반 비이소시아네이트 폴리우레탄(NIPU)은 콩기름의 높은 분자량과 불규칙한 구조 때문에 높은 강성을 달성하는 데에 한계를 가진다. Intersegmental order를 형성하여 강성 특성을 구현하기 위해 poly(2-aminoethylmethacrylate-ran-ethylmethacryate) (poly(AEMA-ran-EMA))를 아민 포함 반응물로 사용하였다. 시차주사열량계 (DSC)를 통해 얻은 유리 전이 온도와 X선 회절 실험(XRD)에서 알아낸 halo peak의 위치를 분석함으로써, 낮은 F$_{AEMA}$ 값을 가진 공중합체로 얻어낸 NIPU가 poly(ethyl methacrylate)와 유사한 intersegmental 구조를 가진다는 사실을 확인하였다. 합성된 NIPU 샘플은 이전의 콩기름 기반 NIPU보다 약 4배 높은 영률과 2배 높은 인장 응력을 나타냈다. 공중합체의 구성 비율은 광범위하고 연속적으로 조절될 수 있으며, 이러한 이점으로 10배 이상 차이 나는 영률과 인장 강도 값을 얻을 수 있음을 확인하였다.