Electron-donating and withdrawing groups substituted Poly (2-methoxy-5-methylsulfinyl-1,4-phenylenevinylene) (PMMSPV) and its copolymers were synthesized via water-soluble precursor pathways and cast into film. The $FeCl_3$-doped PMMSPV exhibits $1.4\times10^{-4}Scm^{-1}$ of electrical conductivity, and the copolymers showed the conductivities at the range of $10^{-4}\sim10^{-1}Scm^{-1}$ depending on their composition. These polymers were characterized with thermogravimetric analysis, UV-visible absorption spectra, and FT-IR analysis. The luminescent property of PMMSPV was also obtained, The maximum emission was observed at 520nm corresponding to green light region. The second order nonlinear optical coefficient of the polymer was characterized with the second harmonic generation method. The measured $d_{33}$ value of PMMSPV was 1.5pm/V with respect to quartz crystal.
전자주게 치환기와 전자끌게 치환기가 도입된 폴리 (2-메특시-5-메틸술피닐-1,4-페닐렌비닐렌)과 공중합체들이 물에 가용한 선중합체를 거쳐서 합성되었다. 이 고분자들은 UV-visible , FT-IR , TGA 등 으로 그 특성이 조사되었다. 고분자들의 전기전도도들이 4-탐침법을 통하여 측정되었으며 PMMSPV 의 경우 $1.5\times10^{-4}Scm^{-1}$의 값을 보였고 공중합체의 경우는 연신된 정도와 공중합체의 조성비에 따라 $10^{-4}\sim10^{-1}Scm^{-1}$의 값을 보였다. 이러한 결과는 전자끌게 치환기인 메틸술피닐기가 PPV의 띠에너지를 상승시켰다는 것을 보여주는 것이라할 수 있다. PMMSPV의 광발광 스펙트럼을 얻은 결과 치환기가 도입되지 않은 PPV보다 약간 단파장쪽으로 이동한 최대발광파장을 보였으며 이 결과도 띠에너지의 상승을 보여준다고 할 수 있다.
전자 쌍극자를 가진 PMMSPV는 적절한 폴링이 이루어질 경우 2차 비선형 광학특성을 보일 것으로 보인다. 2차 비선형광학계수를 2차좝파 방법으로 측정하였으며 측정된 $d_{33}$ 값은 1.5pm/V이다.