Shape memory polymer is a stimuli-responsive polymer which can change its shape when exposed to the external stimuli and have various applications. Recently, with the help of the advances in nano-lithography fabrication techniques, polymers having three dimensional structures with few hundred nanometers have been fabricated and its mechanical responses are reported. But due to the limitations of the fabrication techniques, functional polymer nanostructures including the shape memory polymer nanostructures are barely reported. In this thesis, cm-scale 3D nanostructured shape memory polymer was successfully fabricated using 3D-photolithography technique and thermo-mechanical properties of the as-fabricated sample was characterized. It is expected that this research will help the future fabrication of various temperature-triggered flexible devices.
형상기억 고분자는 외부의 자극을 통해 모양이 변화할 수 있는 고분자로, 다양한 응용 분야를 가지고 있다. 최근, 포토리소그래피 공정의 발달로 수백 나노 미터 정도의 삼차원 구조를 지니는 고분자들이 제작되었고 기계적 물성들이 보고되었으나, 아직 형상기억 고분자를 비롯한 기능성 고분자로 만들어진 나노 구조는 기존 제작 방식의 한계로 거의 보고되지 않은 상황이다. 본 연구 논문에서는 삼차원 포토리소그래피 공정을 응용하여 삼차원 나노 구조를 가지는 형상기억 고분자를 제작하였고 제작된 시편의 열-기계적 물성을 고온 인장 실험을 통해 확인하였다. 본 연구는 온도를 이용하여 작동하는 다양한 연성 소자의 개발에 도움을 줄 것으로 기대된다.