Hybrid supercapacitor using metal oxide and graphene improves the specific capacitance, due to the synergistic effects between both materials. Herein, we demonstrate a facile approach for preparing the hybrid composite electrodes with outstanding areal capacitance and cyclic stability by decoration of SnO2 nanoparticles on vertically-aligned graphene (VAG). VAG electrodes are prepared by electrochemical anodization of graphite foil. SnO2 decorated VAG electrodes (SnO2@VAG) are fabricated by sonication-assisted sequential chemical bath deposition process. Hybrid supercapacitor using SnO2 decorated VAG electrodes shows an excellent areal capacitance (2.26 Fcm-2) and cyclic stability of 90 % after 2000 cycles. We believe that the fabrication of SnO2@VAG may be a significant contribution to the development of high-performance supercapacitors industry.
금속 산화물과 그래핀을 사용하는 하이브리드 슈퍼 커패시터는 두 재료 간의 시너제틱 효과가 일어나 정전용량이 크게 향상된다. 본 연구는 수직 정렬 그래핀 (VAG)의 표면에 산화주석 나노입자를 도포하여 하이브리드 복합전극을 합성하는 손쉬운 제조법을 개발하였다. VAG는 흑연 포일을 전기화학적 양극산화하여 제조한다. 산화 주석 나노입자가 도포된 VAG 복합 전극 (SnO2@VAG)은 초음파 환경에서 VAG에 화학 용액 증착법을 실시하여 제조한다. SnO2@VAG 전극을 이용해 제조된 하이브리드 슈퍼커패시터는 우수한 정전 용량과 뛰어난 주기 안정성을 보여주었다. 이러한 하이브리드 전극 제조법은 고성능 슈퍼커패시터 산업 발전에 많은 기여를 할 수 있을 것으로 예상한다.