In the present study, carbonyl iron powder (CIP)-embedded carbon fiber-reinforced polymer (CFRP) was fabricated with different CIP contents (i.e., 0, 100, 200, and 300 wt%). The effects of CIP contents on the electromagnetic interference (EMI) shielding capabilities of the fabricated composites were observed. The test results exhibited that the AC conductivity of the fabricated composites was improved as the increasing of the CIP contents, and it led to the improvement on the EMI shielding capability. In addition, the mechanical properties of the fabricated composites were discussed in terms of the tensile strengths and young’s modulus, and they were analyzed with the microstructural images taken via SEM and EDS observations. Lastly, the fabricated composites were coated onto the cement mortar, and the applicability as EMI shielding composites in civil structures was investigated.
본 연구에서는 CIP (carbonyl iron powder)가 내장된 탄소 섬유 강화 고분자 복합재 (CFRP)를 다양한 CIP 함량 (즉, 0, 100, 200 및 300 중량 %)으로 제작하였다. 제작된 복합재료의 전자기파 간섭 (EMI) 차폐 능력에 대한 CIP 함량의 영향을 확인하였다. 실험 결과는 CIP 함량이 증가함에 따라 제작된 복합재료의 AC 전도도가 향상되었으며, EMI 차폐능력이 향상되는 것으로 확인되었다. 또한 제작된 복합재료의 기계적 특성을 인장강도 측면에서 논의하고 SEM 및 EDS 관찰을 통해 촬영한 미세구조 이미지로 분석하였다. 마지막으로 제작된 복합재를 시멘트 모르타르에 코팅하고 건축 구조물에서 EMI 차폐 복합재로서 적용 가능성을 조사하였다.