Perovskite nanocrystals are excellent photoluminescent materials as materials having high luminous efficiency and narrow emission line width, but have low structural stability and do not maintain good optical properties for a long time. In this paper, we introduced silica-like siloxane resin to synthesize perovskite NCs/siloxane composite film passivated by chemical bonds. The composite films were tested for photoluminescence stability by observing changes in PL quantum yield in ambient at RT, in water, at high temperature and high humidity condition, and at high temperature and low humidity condition. The composite films showed long-term emission stability over 60 days. And PL QY of the film was observed to be greatly increased in the presence of water. The fluorescence lifetime spectrometry analysis on film allowed monitoring the lifetime of the composite film was greatly increased, and it was confirmed that the trap sites were suppressed by water. This means that the degradation of the perovskite NCs was prevented due to the high stability of the composite film in water, and the recovery effect of water was acted on the composite film.
페로브스카이트 나노입자는 높은 발광 효율과 좁은 발광 선폭을 갖는 재료로서 우수한 광발광 재료이나, 구조 안정성이 낮아 좋은 광 특성을 장기간 유지하지 못한다. 본 논문에서는 실리카와 유사한 구조를 갖는 실록산 레진을 도입해, 화학적 결합으로 패시베이션 된 페로브스카이트 나노입자/실록산 복합 필름을 합성했다. 복합 필름으로 상온의 대기 조건, 물에 담근 조건, 고온 고습 및 고온 저습 조건에서 양자 효율의 변화를 통한 안정성 테스트를 진행했으며, 복합 필름은 60일 이상의 장기간 발광 안정성을 나타냈다. 그리고, 안정성 테스트 시 물이 있는 조건에서 필름의 양자효율이 크게 증가되는 것을 관찰하였다. 수명측정형광분광법을 통해 복합 필름에서, 광 발광 수명이 크게 증가되는 것을 통해 물에 의해 발광 트랩이 억제되었음을 확인했다. 이는 복합 필름의 물에 대한 높은 안정성으로 인해 페로브스카이트의 구조 분해가 방지되면서 물의 회복 효과가 작용했음을 보여준 결과이다.