Flexible thin-film solar cells are an essential task of second-generation solar cells. In this study, the solar cell was fabricated by using $Cu_2ZnSnSe_4$(CZTS) consisted of earth-abundant elements as an absorber layer and Titanium (Ti) foil as a substrate to make low cost flexible thin-film solar cell. In the process, the CZTS deposition conditions were adjusted to control the secondary phases and defects. To analyze the effects of Soda-lime glass and Ti substrates on CZTS solar cells, the characteristics of the two solar cells were compared. Ti substrates have found that higher temperature annealing is required. As a result, it was observed that there is a deeper energy trap and lower carrier concentration in the CZTS solar cell of the Ti substrate by comparing the characteristics of the solar cells of two optimized substrates. This is expected to be due to the lack of sodium. J-V and external quantum efficiency (EQE) measurement, capacitance-voltage (CV) measurements, and admittance spectroscopy (AS) measurements were used for analysis.
유연한 박막 태양 전지는 2 세대 태양 전지의 필수 과제이다. 본 연구에서는 저비용의 유연한 박막 태양 전지를 만들기 위해 흡수층으로 범용성 원소로 구성된 $Cu_2ZnSnSe_4$(CZTS)와 기판으로 티타늄(Ti) 포일을 사용하여 태양 전지를 제작 하였다. 이 공정에서, CZTS 증착 조건은 2차상 및 결함을 제어하도록 조정되었다. CZTS 태양 전지에 성능에 대한 소다-석회 유리 및 티타늄 기판의 효과를 분석하기 위해, 두 태양 전지의 특성을 비교 하였다. Ti 기판은 보다 높은 온도에서의 열처리 조건을 요하다는 것을 발견하였다. 결과적으로, 최적화 된 두 기판의 태양 전지의 특성을 비교함으로써 티타늄 기판에 제작된 CZTS 태양 전지가 더 깊은 에너지 트랩 및 더 낮은 캐리어 농도를 가지는 것을 밝혀내다. 관찰되었다. J-V 및 외부 양자 효율 (EQE) 측정, 전기용량-전압 (CV) 측정 및 어드미턴스 분광법 (AS) 측정을 태양전지 성능 분석에 사용했다.