High Entropy Alloys (HEAs) have higher configuration entropies than conventional alloys because they have more than 5 metallic elements as principal elements with an equiatomic or near equi-atomic ratio. The high configuration entropy makes HEAs form a simple solid solution phase such as BCC or FCC. HEAs are promising candidates for industrial structural materials due to their excellent mechanical properties. Despite the excellent mechanical properties, it is needed to apply various strengthening mechanisms to HEAs in order to broaden the application area of HEAs by improving its mechanical properties. In this study, CoCrFeMnNi HEAs with 0.5 wt% of $Y_2O_3$ were fabricated to make an oxide dispersion strengthened (ODS) HEA. ODS-HEA powder particles were prepared under various process conditions. To investigate the effects of milling and sintering process parameters, the microstructural analysis of powder and sintered bulk samples was conducted. A small angle neutron scattering (SANS) analysis was conducted to perform the statistical analysis of nano-sized oxide particles in ODS-HEA powder and sintered bulk samples under various cryo-milling and heat treatment
고엔트로피 합금은 일반적인 상용 합금과는 달리 5가지 이상의 구성원소가 동등한 분율 또는 비슷한 분율로 구성되어 높은 구성엔트로피를 특성으로 갖는다. 높은 구성엔트로피로 인하여 단상을 형성하며 우수한 기계적 물성을 가지고 있어 다양한 산업구조재로 활용 될 수 있을 것으로 기대되고 있으며 활발히 연구가 진행되고 있다. 하지만 고엔트로피 합금의 조사특성은 아직 확고히 정립되지 않았다. 고엔트로피 합금의 적용 영역을 넓히고 우수한 기계적 특성을 유지 또는 개선시키기 위하여 여러 강화기구들을 고엔트로피 합금에 적용하는 것이 고려되고 있다.
본 연구에서는, CoCrFeMnNi 계 고엔트로피 합금을 이용하여 $Y_2O_3$의 첨가를 통한 산화물 분산강화 고엔트로피 합금을 제조하였다. 산화물 분산강화 고엔트로피 합금 분말은 다양한 공정 조건하에서 제조 되었으며, 기계적 합금화 및 소결과정의 여러 공정변수들이 분말에 미치는 영향을 분석 하기 위해 분말과 소결체의 미세조직 분석을 진행하였다. 여러공정변수에 따라 생성된 기지 내 산화물의 통계적 결과를 도출하고자 중성자소각산란 실험을 진행하였다. 본 연구의 결과는 고엔트리피합금의 산화물 분산강화 기구의 형성과정을 이해하는데 기여할 것으로 기대된다.