Urushiol is a main component of lacquer sap, and has useful properties such as good durability, thermal stability, and antimicrobial activity. Since lacquer sap causes skin allergy, it is necessary to polymerize urushiol monomer in order to use it as an antimicrobial material. Conventional method of polymerizing urushiol is making film-type urushiol polymer through laccase catalytic reaction. This method requires a grinding process to make polymerized urushiol film into powder. In this study, we developed emulsion polymerization method to produce urushiol powder without grinding process. The particle size of urushiol powder could be controlled by introducing emulsion polymerization. The particle size was monitored under different operational condition such as HLB value of surfactant, surfactant concentration, and agitation speed. Experimental investigations showed that the particle size decreased with increasing HLB value of surfactant, surfactant concentration, and agitation speed. The monodispersed urushiol powder was obtained at a stirring rate above 12,000 rpm, showing the minimum size of 63.2 ± 8.6 μm.
우루시올은 옻나무 수액의 주성분으로 우수한 내구성, 열 안정성, 및 항균성과 같은 유용한 특성을 가지고 있다. 옻나무 수액은 피부 알레르기를 유발하는 단점을 가지고 있으므로, 이를 항균성 물질에 이용하기 위하여 단량체를 중합 반응으로 고분자화 하여야 한다. 기존 우루시올을 중합하는 방법은 라카아제 촉매 반응을 통해 필름 타입의 중합체를 만드는 것으로 경화된 우루시올을 분말로 만들기 위해서 분쇄 공정을 필요로 한다. 본 연구에서는 분쇄 공정 없이 우루시올 분말을 생산하기 위해 에멀젼 중합법을 개발하였다. 에멀젼 중합법을 도입함으로써 우루시올 분말의 입자를 조절할 수 있었다. 유화제의HLB값과 농도, 그리고 교반 속도 조건을 변화시키면서 분말 크기에 대한 영향을 조사하였고 HLB 값 및 농도, 교반 속도가 증가함에 따라 입자 크기는 감소하는 것을 관찰하였다. 12,000rpm 이상의 교반 속도에서 단분산 우루시올 분말을 얻을 수 있었으며, 단분산 우루시올 분말의 최소 크기는 63.2 ± 8.6 μm이었다,