Poly(3-hexylthiophene) (P3HT) has received a great deal of attention in organic electronic field in that it has obviously controllable morphology and high crystallinity to be applied as various organic electronic applications. Nevertheless, the mechanical weakness of polymer film was the ultimate limitation of commercialization. Therefore, we suggested that the regioregular-regiorandom P3HT regioblock copolymer approach by using living characteristics of GRIM polymerization to obtain both high electrical and mechanical properties. We synthesized the series of P3HTs composed of identical length of crystallizable regioregular block and different length of amorphous regionrandom block in each polymer. Then, we produced well-defined nanowires using the solution self-assembly of regioregular-regiorandom P3HT regioblock copolymer to construct highly ordered electron channel. We observed the small amount of regiorandom block facilitated the formation of longer assembly structure and excessive length of that block hindered the growth of assembly. This was corresponded with the charge carrier mobility. The hole mobility was improved as a degree of order after progressed with solution assembly and it depended on the length of assembly structures.
Poly (3- hexylthiophene) (P3HT)는 다양한 몰폴로지 조절과 높은 결정성이란 장점을 기반으로 유기 전자 분야에서 많은 주목을 받았다. 그러나 고분자 필름의 낮은 기계적 안정성 때문에, 상용화에 제약을 받아왔다. 따라서, 우리는 높은 전기적 및 기계적 성질을 얻기 위해 GRIM 중합의 리빙 특성을 이용하여 regioregular-regiorandom P3HT regioblock copolymer 를 합성하였다. 각 고분자는 모두 동일한 길이의 결정성을 가지는 Regular 블록과, 서로 다른 길이의 유연성을 가지는 Random 블록으로 이루어져 있다. 그 후, 용액 내 자가조립을 통해서, 잘 배열된 전자 채널 구조인 나노와이어를 형성시켜 주었다. 그 결과, 소량의 Random 블록은 나노와이어의 형성을 안정화 시켜 매우 긴 자가조립구조를 만들었으며, 너무 긴 길이의 Random 블록은 자가조립 형성을 방해해서 짧은 형태의 구조를 형성시켰다. 또한 이 결과는 캐리어 이동도와도 밀접한 관련이 있었다. 이동도는 나노와이어의 길이와 비례관계를 가졌으며, 긴 길이의 자가조립 구조는 높은 전기적 특성을 나타내었다.